Abstract:Microstructure evolution and fracture behavior of Mg-9.5Gd-0.9Zn-0.5Zr alloy subjected to different heat treatments were systematically investigated using SEM and TEM as well as tensile testing. It was found that the microstructure of the as-cast alloy consisted of α-Mg matrix, net-like eutectic compounds (α-Mg + Mg3 (Gd, Zn)), cubic GdH2 phases and lamellar 14H LPSO phases. After solution treated at 515 °C for 24 h, two different cooling processes were used to elucidate the effect of cooling rates on the precipitation microstructure. With a hot water quenching, those secondary phases were completely dissolved. Instead, grey-like patches were observed within the α-Mg matrix, which were proposed to be rod-like Zn2Zr3 phases around the α-Zr particle. In contrast, with a furnace cooling, the formation of 14H LPSO and several cubic Mg3 (Gd, Zn) phases was observed. Furthermore, after hot water quenching, the subsequent ageing treatment parameters were also optimized to be 225 °C for 48 h. In the peak-aged condition, a denser and uniform distribution of basal precipitates γ″ and several basal precipitates γ′ together with Zn2Zr3 and ZnZr2 phases were observed. The samples after the solution treatment (for both hot water quenching and furnace cooling) showed a much higher ductility than the as-cast alloy, while the tensile yield strength (TYS) and ultimate tensile strength (UTS) remained unchanged. After the peak-ageing, a significant increase in the TYS and UTS but a great loss in ductility was observed. In the as-cast alloy, the initiation of microcracks occurred from the net-like eutectic compounds, which was believed to be one of the most important reasons for the tensile fracture, and showed a co-existence of intergranular and transgranular fracture behavior. After the solution treatment, with a hot water quenching, the fracture can be mainly related with failures along contraction twins, and then showed a transgranular fracture behavior. While, with a furnace cooling, due to the presence of the kinked 14H LPSO phases, the fracture was caused by the broken of 14H LPSO phases, and then lead to a transgranular fracture. The peak-aged alloy exhibited a brittle intergranular fracture, which can be related with failures along soft precipitation free zones (PFZs).

Damage Morphology Study of High Cycle Fatigued As-Cast Mg–3.0Nd–0.2Zn–Zr (wt.%) Alloy

Fatigue deformation mechanism of the Mg–Nd alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

Fatigue characteristics of a newly developed laser powder bed fused scandium-free Al-Mg-Zr-Mn alloy

Quantitative assessment of the microstructural factors controlling the fatigue crack initiation mechanisms in AZ31 Mg alloy

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

High-Cycle Fatigue of Mg–6Gd–3Y–0.5Zr Cast Magnesium Alloys

Damage evolution of extruded magnesium alloy from deformation twinning and dislocation slipping in uniaxial stress-controlled low cycle fatigue

In-situ synchrotron X-ray tomography investigation of damage mechanism of an extruded magnesium alloy in uniaxial low-cycle fatigue with ratchetting

Role of defects on the high cycle fatigue behavior of selective laser melted Al–Mg–Sc–Zr alloy

Effect of Microstructure on Tensile and Fatigue Properties of Cast Mg–10Gd–2Y–0·5Zr Alloy

Crystal plasticity modeling of low-cycle fatigue behavior of an Mg-3Al-1Zn alloy based on a model, including twinning and detwinning mechanisms

Failure Behavior of High Pressure Die Casting AZ91D Magnesium Alloy

Mechanical properties and fracture behavior of Mg–3Al–1Zn alloy under high strain rate loading

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Microstructure evolution and fracture behavior of Mg-9.5Gd-0.9Zn-0.5Zr alloy subjected to different heat treatments

Grain size and orientation affected deformation inhomogeneity and local damage of hot-deformed Al-Zn-Mg alloy

Effects of laser shock processing, solid solution and aging, and cryogenic treatments on microstructure and thermal fatigue performance of ZCuAl10Fe3Mn2 alloy

Relationship Between the Fatigue Behavior and Grain Structures of an As-Extruded Mg-6.2%Zn-0.6%Zr (in Wt.%) Alloy

Experimental and numerical analysis of cyclic deformation and fatigue behavior of a Mg-RE alloy