Abstract:Intumescent flame retardants (IFR) with phosphorus (P)/nitrogen (N)-containing diphenols (DH, DV and DS) were synthesized from p-hydroxybenzaldehyde (H), vanillin (V) and syringaldehyde (S) with different methoxyl groups on its aromatic ring. The FTIR, 1H NMR, 13C NMR, XPS methods were used to characterize the structures of IFR, and LOI, CCT, SEM, TG methods were used to investigate the flame retardancy and thermal stability of rigid polyurethane (RPU) foams when the three IFR were incorporated into RPU foams. Compared with H, V and S, the DH, DV and DS FTIR spectra showed absorption peaks at 3450 cm−1, 1160 cm−1, and 1222 cm−1, 1050 cm−1 and 740 cm−1, respectively, which attributed to NH, CN, and P = O, P-O, P-C groups. The 1H NMR spectra of DH, DV and DS showed proton signals at 4.8 and 6.0 ppm, which were corresponding to H1 and H2 of CN groups, and corresponding C1 signal appeared around 62.3 ppm in the 13C NMR spectra. The XPS spectra of DH, DV, DS showed peaks at 285, 398 eV and 133.5, 532 eV, which may be due to corresponding C1s, N1s of CN groups and P2p and O1s of P-O-C groups, respectively. These results indicated that the target compounds P/N-containing diphenols DH, DV and DS were synthesized successfully. Flame retardancy index (FRI) values of RPU-DH, RPU-DV, and RPU-DS were 2.33, 2.30 and 2.43, respectively, suggesting that DH, DV, and DS were good flame retardant additives. The THR and HRR values of RPU-DH, RPU-DV, RPU-DS foams were much lower than that of RPU foam. The fire growth rate (FIGRA) of RPU-DH, RPU-DV, and RPU-DS was 29.4%, 30.3%, and 24.4% lower comparing to RPU foam. The LOI value of RPU foam was 19%, while LOI values of RPU-DH, RPU-DV and RPU-DS foams increased to around 26%. These results suggested that the flame retardancy of RPU foams were improved by incorporating DH, DV, and DS. Compared with RPU foam, the CY600 of RPU-DH, RPU-DV and RPU-DS foams increased by 215.2%, 152.2% and 195.6%, respectively, and the char residue after CCT were much compact and homogeneous, which could reduce heat and mass transfer, protecting underlying materials from further combustion in a fire. In conclusion, the P/N-containing diphenols DH, DV and DS were synthesized successfully, and they were good flame retardant additives. The char residue of RPU-DH, RPU-DV and RPU-DS foams increased remarkably, and formed compact and homogeneous char layer. The flame retardancy and thermal stability of RPU-DH, RPU-DV, RPU-DS foams were improved by incorporating DH, DV, and DS.

Effects of a Novel Phosphorus–nitrogen Flame Retardant on Rosin-Based Rigid Polyurethane Foams

Effects of Novel Phosphorus-Nitrogen-containing DOPO Derivative Salts on Mechanical Properties, Thermal Stability and Flame Retardancy of Flexible Polyurethane Foam

Highly-efficient Reinforcement and Flame Retardancy of Rigid Polyurethane Foam with Phosphorus-Containing Additive and Nitrogen-Containing Compound

Flame-retarded polyurethane foam conferred by a bio-based nitrogen‐phosphorus-containing flame retardant

Biobased Phosphorus Siloxane-Containing Polyurethane Foam with Flame-Retardant and Smoke-Suppressant Performances

Halogen-free Flame-Retardant Rigid Polyurethane Foam with a Nitrogen–phosphorus Flame Retardant

Phosphorus and Nitrogen-Containing Polyols: Synergistic Effect on the Thermal Property and Flame Retardancy of Rigid Polyurethane Foam Composites

Thermal decomposition and flammability of rigid PU foams containing some DOPO derivatives and other phosphorus compounds

The Preparation and Properties of Flame-Retardant Polyisocyanurate–polyurethane Foams Based on Two DOPO Derivatives

A reactive melamine-DOPO based flame retardant for superior thermal stability and flame retardancy in rigid polyurethane foam

Synthesis of reactive DOPO-based flame retardant and its application in rigid polyisocyanurate-polyurethane foam

Synthesis of a Novel Flame Retardant Based on DOPO Derivatives and Its Application in Waterborne Polyurethane

Synthesis of a Novel Phosphorus and Nitrogen-Containing Flame Retardant and Its Application in Rigid Polyurethane Foam with Expandable Graphite

Environmentally Friendly Flame-Retardant and Its Application in Rigid Polyurethane Foam

Research on Properties of Rigid Polyurethane Foam with Heteroaromatic and Brominated Benzyl Polyols

The synthesis and characterization of a DOPO derivative bearing an active terminal epoxy group: e-DOPO and its application in rigid polyurethane foam

Synthesis of phosphorus/nitrogen containing intumescent flame retardants from p-hydroxybenzaldehyde, vanillin and syringaldehyde for rigid polyurethane foams

Reactive flame-retardants prepared by transesterification between erythritol and dimethyl methyl phosphonate for rigid polyurethane foams

Flame Retardancy and Physical Properties of Rigid Polyurethane Foam Containing Phosphorus Flame Retardants

The Thermal Properties and Flame Retardancy of 9,10-Dihydro-9-oxa-10-phosphaphenanthrene 10-Oxide (dopo)–mg/polyisocyanurate–polyurethane Foam Composites

Preparation and intrinsical flame resistance of reed-based polyurethane foam modified by 9,10-dihydro-9-oxa-10 phosphaphenanthrene 10-oxide