Abstract:A series of Mn-doped K-Co-Mo catalysts were prepared by a sol-gel method. The catalyst structure was well characterized by X-ray diffraction, N-2 physisorption, NH3 temperature programmed adsorption, in situ diffuse reflectance infrared Fourier transform spectroscopy, and X-ray absorption fine structure spectroscopy. The catalytic performance for higher alcohol synthesis from syngas was measured. It was found that the Mn-doped catalysts exhibited a much higher activity as compared to the unpromoted catalyst, and in particular the C2+ alcohol selectivity increased significantly. The distribution of alcohol products deviated from the Anderson-Schulz-Flory law. The portion of methanol in total alcohol was suppressed remarkably and the ethanol became the predominant product. Characterization results indicated that the incorporation of Mn enhanced the interaction of Co and Mo and thus led to the formation of Co-Mo-O species, which was regarded as the active site for the alcohol synthesis. Secondly, the presence of Mn reduced the amount of strong acid sites significantly and meanwhile promoted the formation of weak acid sites, which had a positive effect on the synthesis of alcohol. Furthermore, it was found that the incorporation of Mn can enhance the adsorption of linear- and bridge-type CO significantly, which contributed to the formation of alcohol and growth of carbon chain and thus increased the selectivity to C2+OH.

CO Hydrogenation to Higher Alcohols over Ni- and Mo-modified Cu/CeO 2 Catalyst

Synthesis of Higher Alcohols from CO 2 Hydrogenation over Mo–Co–K Sulfide-Based Catalysts

Synthesis of higher alcohols by CO hydrogenation on a K-promoted Ni–Mo catalyst derived from Ni–Mo phyllosilicate

Effect of KCoMoS2 Catalyst Structures on the Catalytic Performance of Higher Alcohols Synthesis via CO Hydrogenation

Influence of Co Modified Mn/Cu/MgO Catalyst on the Synthesis of Mixed Alcohols from Syngas

Effect of Cerium Addition on the Catalytic Performance of Cu-Fe/Sio2 for the Synthesis of Lower Alcohols from Syngas

Production of Hydrogen by Steam Reforming of Methanol on CeO2 Promoted Cu/Al2O3 Catalysts

Effect of the promoter and support on cobalt-based catalysts for higher alcohols synthesis through CO hydrogenation

Cu-Promoted Iron Catalysts Supported on Nanorod-Structured Mn-Ce Mixed Oxides for Higher Alcohol Synthesis from Syngas

Cu/ZnO/CeO2 Supported on MOF-5 as a Novel Catalyst for the CO2 Hydrogenation to Methanol: A Mechanistic Study on the Effect of CeO2 and MOF-5 on Active Sites

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation

Hydrogenolysis of Glycerol Aqueous Solution to Glycols over Ni–Co Bimetallic Catalyst: Effect of Ceria Promoting

Ternary copper–cobalt–cerium catalyst for the production of ethanol and higher alcohols through CO hydrogenation

Synthesis-Gas Production from Methane over Ni/CeO2 Catalysts Synthesized by Co-Precipitation Method in Different Solvents

Methanol Synthesis from CO2 Hydrogenation over CuZnCeTi Mixed Oxide Catalysts

Preferential Oxidation of CO and Its Subsequent Methanation in H2-rich Gas over CuO–NiO/CeO2 Catalysts

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

CO2 Hydrogenation to Methanol over Bimetallic Pd-Cu Catalysts Supported on TiO2-CeO2 and TiO2-ZrO2

Effect of Mn Promoter on Structure and Performance of K-Co-Mo Catalyst for Synthesis of Higher Alcohols from CO Hydrogenation

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts