Abstract:High-quality zeolite silicalite-1 membranes with a large area (78.5cm2) were successfully prepared on porous, tubular stainless steel (PTSS) supports with optimized synthesis solution composition by a two-stage varying-temperature in situ synthesis. Compared with the synthesis at constant temperature (one-stage), the two-stage varying-temperature in situ synthesis (TSVTS) generated a thin and dense membrane, since a large number of new nuclei could form at low temperature, while the crystallization temperature was rapidly changed to a high temperature after completion of the nucleation period, a thin and continuous membrane would quickly formed on the support by the nuclei regrowth. The membranes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single-gas permeation. These results indicate that the membranes prepared by the TSVTS method exhibit high gas permeation performance and good reproducibility. H2 permeance and H2/n-C4H10 selectivity of the membranes by TSVTS method reached to 12.25×10−7mol/(m2sPa) and 46.1, respectively. And the yield of high-quality membranes with perm-selectivity of H2/n-C4H10 larger than 25 (which is almost five times as large as the Knudsen factor) as a quality criterion reached to 70% of all preparations. By comparison of their permeability and reproducibility with those reported in the literature, it was revealed that the prepared membranes by TSVTS method were of good quality. Moreover, their thermal stability were tested in a gas mixture of ethylbenzene and hydrogen at high temperature, for an example, the membrane having the separation selectivity of hydrogen and ethylbenzene mixture as high as 190 is stable after 80h of run at 400°C, suggesting the membrane is thermally durable for long time operation.

Synthesis of Silicalite-1 Membrane with High-Thermal Stability on Silica Tubes by<i> In Situ</i> Hydrothermal Synthesis

A Novel Method to Synthesize High Performance Silicalite-1 Membrane

Effects of aging on the synthesis and performance of silicalite membranes on silica tubes without seeding

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Preparation of Silicalite-1 Membranes on Stainless Steel Supports by a Two-Stage Varying-Temperature in Situ Synthesis

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Preparation and Pervaporation Performance of Silicalite-1 Zeolite Membrane with a Two-stage Temperature-varied Hydrothermal Technique

Synthesis of silicalite-1 membrane with two silicon source by secondary growth method and its pervaporation performance

SYNTHESIS OF SILICALITE-1 MEMBRANE BY A NOVEL EMBELLISHING METHOD AND ITS GAS PERMEANCE

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Preparation of silicalite-1 zeolite membrane by a two-stage-varying temperature synthesis for pervaporation separation of ethanol from water

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Synthesis and Low-Temperature Detemplation of High-Silica Mfi Zeolite Membranes

Fast synthesis of thin Silicalite-1 zeolite membranes at low temperature

Preparation and characterization of silicalite-1 membrane on a silicalite-1/TiO2 composite layer

Preparation and characterization of silicalite-1 membrane by counter-diffusion secondary growth

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Synthesis and structural analysis of Silicalite-1 membranes by coating technique with nanosized seed

Synthesis and property of silicalite-1 membranes by restricting growth method with dilute solution