Abstract:In this study, the effect of TiCN and WC-Co coatings on the tribological performance of spheroidal graphite cast iron materials was investigated by wear tests under dry and lubricated conditions. The mechanical and physical effects of the coating processes were analysed by microhardness measurements and visual methods (SEM, EDX, XRD). The tribological effect of WC-Co and TiCN coated specimens were investigated by ball-on-plate wear tests carried out under dry and boron oil emulsion (5% concentration) conditions at 50 N load and 60 rpm sliding speed parameters. The friction coefficient and wear volume results were obtained to investigate the effect of the coating process and boron oil emulsion on friction and wear behaviour. The wear mechanisms were determined with SEM images obtained from the worn surfaces and surfaces analysed elementally with EDX images. Additionally, surface morphology was examined with surface roughness measurements and 2D–3D topography images. According to the microhardness measurement results, it was observed that the spheroidal graphite cast iron with 290 HV hardness reached 1559 HV with TiCN coating and 1440 HV with WC-Co coating. According to the wear test results, it was determined that TiCN and WC-Co coatings decreased the friction coefficient by 32.51% and 12.80%, respectively. When the effect of boron oil usage compared to dry environmental conditions, it was concluded that the friction coefficient and wear volume decreased by a maximum of 54.80% and 53.70%, respectively. Additionally, the roughness values decreased in the experiments where the boron oil emulsion was used. However, although the TiCN coating improved the surface quality, the WC coating negatively affected the surface quality. Surface form images obtained with 2D and 3D topography also support the alteration in roughness values.

Study on Wear Mechanism of Chromium Carbide Coating Reinforced Cast Iron Cylinder Sleeve

Analysis on Wear Properties and Impact Factors for Si3N4 Ceramic Mated with Chilled Cast Iron

High-frequency and Overloading Friction Wear Test of Cermet Coated Engine Cylinder Liner

Tribological Performance of Chromium Nitrided Piston Ring Coating

Wear Performance of Cast Iron Piston Rings Strengthened by Laser

Reciprocating sliding friction behavior and wear state transition mechanism of cylinder liner and piston ring

Researches of Cast Iron Piston Rings Strengthened by Laser

The investigation on friction and wear properties of cast iron matrix surface compact vanadium carbide layer

Low and high temperature effects on friction and wear performance of Cr-plated cylinder liner

Investigation of wear behavior of carbide based coated rolling roll materials under dry and lubricated conditions

Emergence of Coated Piston Ring Scuffing Behavior on an Application-Oriented Tribological Model Test System

Wear and Friction Behavior of Plasma Sprayed NiCrMo-NiCrBSi Alloy Anti-Friction Coatings

A review on preparation process and tribological performance of coatings for internal combustion engine piston ring

Study on salt spray corrosion and friction wear performance of CrN coated cemented carbide sealing ring

Wear Resistance Analysis of Hardening Materials for Engine Cylinder

Evaluation of the Microstructure, Tribological Characteristics, and Crack Behavior of a Chromium Carbide Coating Fabricated on Gray Cast Iron by Pulsed-Plasma Deposition

Study on Friction and Wear Performance of Sliding Metal Seal Materials Under Reciprocating Motion

A comparative investigation on wear behaviors of physical and chemical vapor deposited bronze coatings for hydraulic piston pump

Sliding Wear of Cast-Iron Coatings and Cast-Iron-cast-iron Pairs in Lubricated Contact

Effect of lubrication on the wear behaviour of CrN coating deposited by PVD process

Synergy Study Between a Lubricant Oil Layer and a Microstructural Graphite to Reduce Friction and Wear of a Thermally Modified Low-Carbon Gray Cast-Iron Cylinder Liner