Abstract:This study examines the wettability behaviour of 304 stainless steel (304SS) and Ti-6Al-4V (Ti64) surfaces after sequential nanosecond (ns) and picosecond (ps) laser texturing; in particular, how the multi-scale surface structures created influence the lifecycle of surface hydrophobicity. The effect of different post-process treatments is also examined. Surfaces were analysed using Scanning Electron Microscopy (SEM), a white light interferometer optical profiler, and Energy Dispersive X-ray (EDX) spectroscopy. Wettability was assessed through sessile drop contact angle (CA) measurements, conducted at regular intervals over periods of up to 12 months, while EDX scans monitored elemental chemical changes. The results show that sequential (ns + ps) laser processing produced multi-scale surface texture with laser-induced periodic surface structures (LIPSS). Compared to the ns laser case, the (ns + ps) laser processed surfaces transitioned more rapidly to a hydrophobic state and maintained this property for much longer, especially when the single post-process treatment was ultrasonic cleaning. Some interesting features in CA development over these extended timescales are revealed. For 304SS, hydrophobicity was reached in 1-2 days, with the CA then remaining in the range of 120 to 140° for up to 180 days; whereas the ns laser-processed surfaces took longer to reach hydrophobicity and only maintained the condition for up to 30 days. Similar results were found for the case of Ti64. The findings show that such multi-scale structured metal surfaces can offer relatively stable hydrophobic properties, the lifetime of which can be extended significantly through the appropriate selection of laser process parameters and post-process treatment. The addition of LIPSS appears to help extend the longevity of the hydrophobic property. In seeking to identify other factors influencing wettability, from our EDX results, we observed a significant and steady rate of increase in the carbon content at the surface over the study period.

Preparation of Hydrophobic and Oleophilic Surface of 316 L Stainless Steel by Femtosecond Laser Irradiation in Water

Fabrication of superhydrophobic stainless steel via hybrid femtosecond laser-chemical method with wear-resistance and anti-corrosion properties

Preparation of superamphiphobic stainless steel surface by laser and perfluorooctanoic acid treatment

Nanosecond Laser Fabrication Of Superhydrophobic Surface On 316l Stainless Steel And Corrosion Protection Application

Superhydrophobic Surfaces Fabricated by Microstructuring of Stainless Steel Using A Femtosecond Laser

Formation mechanism of superhydrophobicity of stainless steel by laser-assisted decomposition of stearic acid and its corrosion resistance

Preparation of Stainless Steel Superhydrophobic Surface and Analysis of Hydrophobic Mechanism

Nanosecond Laser Fabrication of Hydrophobic Stainless Steel Surfaces: The Impact on Microstructure and Corrosion Resistance

Biomimetic fabrication of robust self-assembly superhydrophobic surfaces with corrosion resistance properties on stainless steel substrate

Fast Reversion of Hydrophility-Superhydrophobicity on Textured Metal Surface by Electron Beam Irradiation

Femtosecond laser surface roughening and pulsed plasma polymerization duplex treatment on medical-grade stainless steel substrates for orthodontic purpose

Long term superhydrophobic and hybrid superhydrophobic/superhydrophilic surfaces produced by laser surface micro/nano surface structuring

Superhydrophobic Surfaces with Micro-/Nano-structures Prepared by Femtosecond Laser

Creation of Superhydrophobic Stainless Steel Surfaces by Acid Treatments and Hydrophobic Film Deposition

Experimental research on the fabrication and wettability of micro- and nano-scale surface textures produced on stainless steel using an ultrafast laser

Preparation of super-hydrophobic surface on stainless steel

Superhydrophobic and Antibacterial Hierarchical Surface Fabricated by Femtosecond Laser

Super-hydrophobicity and corrosion resistance of laser surface textured AISI 304 stainless steel decorated with Hexadecyltrimethoxysilane (HDTMS)

Nanosecond laser etching for enhanced multi-scale layered micro-nano superhydrophilic 304 stainless steel surface

Laser-Assisted Structures for Efficient Fluid Management on Stainless Steel Surfaces

Wettability Behaviour of Metal Surfaces after Sequential Nanosecond and Picosecond Laser Texturing