Manganese Dissolution from LiMn 2 O 4 Cathodes at Elevated Temperature: Methylene Methanedisulfonate As Electrolyte Additive

Renheng Wang,Xinhai Li,Zhixing Wang,Huajun Guo

DOI: https://doi.org/10.1007/s10008-015-2998-1

IF: 2.747

2015-01-01

Journal of Solid State Electrochemistry

Abstract:Diethyl carbonate (DEC) electrolyte decomposition reactions resulting from PF 5 attacked produce HF by several side reaction steps. The resulting HF can dissolve the Mn from spinel-type lithium manganese oxide (LiMn 2 O 4 ). To verify that methylene methanedisulfonate (MMDS) suppress Mn 3+ dissolution mechanism of lithium manganese oxide spinel cathode using methylene methanedisulfonate as electrolyte additive at elevated temperature, a DEC-based electrolyte using MMDS as electrolyte additive is developed in this work. The linear sweep voltammetry (LSV) indicates the start oxidation potential of the electrolyte with 0.5 wt% MMDS is around 3.83 V (vs. Li/Li + ), which is lower than the control (4.12 V). Self-discharge and inductively coupled plasma-atomic emission spectrometry (ICP-AES) reveal that Mn 3+ dissolution from the spinel cathode is hindered. The results of electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS) demonstrate that MMDS would help to form the stable passivation film, which would effectively suppress to oxidize the control electrolyte solvents and HF generation is suppressed, and result in less Mn 3+ dissolution from the spinel cathode.