Abstract:A rapid thermal processor (RTP) device as well as quenching technique is employed to systematically investigate the effect of surface heat transfer coefficient (h) gradient on thermal shock failure of a hot-pressed ZrB2-based ceramic. Two typical kinds of quenchant with different surface h gradients during quenching tests, water and boiling water, are used for this study. When water as the cooling medium, two different cooling modes of indirect contact cooling by RTP device and direct contact cooling by quenching are also studied. The experimental results and related numerical simulations illustrate that surface h gradient plays an important role in thermal shock failure. This study confirms the previous presumption that the combination of body temperature gradient and surface h gradient leads to thermal stress damage and thermal shock failure. Under water quenching condition, water phase changes form bubbles randomly and produce great surface h gradient. Accordingly, critical body temperature gradient (V(max)(c)) is small (similar to 270 degrees C s(-1)). Under aqueous polymer quenching condition, the introduction of polymer chains into water lowers the random formation of steam bubble and mediates the surface h gradient. The corresponding V(max)c hence become larger (similar to 500 degrees C s(-1)) Under boiling water quenching condition, there is no surface h gradient and V(max)(c) is even larger (>600 degrees C s(-1)). This study provides useful complementary information for understanding the thermal shock behavior and gives suggests for predicting materials performance in actual service.

Effect of the Cooling Medium Temperature on the Thermal Shock Resistance of Ceramic Materials

An Aqueous Polymer Quenching Medium for Instantaneous Thermal Shock Cooling Rate Study of Ceramic Materials

Evaluations of cooling rate and initial temperature on thermal shock behavior of ZrB 2 -SiC ceramic

Effect of Surface Heat Transfer Coefficient Gradient on Thermal Shock Failure of Ceramic Materials under Rapid Cooling Condition

Thermal shock resistance of ceramics with temperature-dependent material properties at elevated temperature

Thermal shock behavior of ZrB2–SiC ultra-high temperature ceramics with addition of zirconia

Thermal Shock Behavior of Zrb2-Sic Ceramics with Different Quenching Media

Thermal Shock Property of ZrB_2-Based Ultra-High Temperature Ceramics

Mechanisms of Thermal Shock Failure for Ultra-High Temperature Ceramic

Thermal Shock Stress Considering Dynamical Behavior for Ultra High Temperature Ceramic

The Influence of Surface Heat Transfer Conditions on Thermal Shock Behavior of ZrB2–SiC–AlN Ceramic Composites

Thermal shock characterization of large size ZrB2 ceramic matrix composite material

Experimental study on the influential factors of thermal shock resistance of ultra-high temperature ceramic composite materials

Thermal Shock Resistance of Porous Ceramic Foams with Temperature-Dependent Material Properties

Prediction of Crack Depth During Quenching Test for an Ultra High Temperature Ceramic

The Thermal Shock Resistance Analysis of Ceramic Foams

Evaluation of Thermal-Shock Fracture-Resistance of Ceramics by Quenching-Small Punch-(Sp) Test

Thermal Shock Behavior of Porous ZrB2–SiC Ceramics

A Multi-Scale Model for Predicting the Thermal Shock Resistance of Porous Ceramics with Temperature-Dependent Material Properties

Mechanism Analysis of Thermal Shock Properties for Zrb2-20%Sicp-10%Aln Ultra-High Temperature Ceramic with the Surface Defects

Thermal shock resistance of ZrC matrix ceramics