Influence behavior and mechanism of crystal orientation of Cu 6 Sn 5 coating on interfacial intermetallic compounds growth in Sn-0.7Cu/Cu solder joint
Zhihang Zhang,Jiawei Qu,Tao Ma,Yue Zhao,Zhongshan Zhou,Jihua Huang,Shuhai Chen,Zheng Ye,Jian Yang
DOI: https://doi.org/10.1016/j.matchar.2024.113832
IF: 4.537
2024-03-18
Materials Characterization
Abstract:Herein, the Cu 6 Sn 5 coatings with principal crystal orientations were prepared on the Cu substrate using magnetron sputtering to inhibit the growth of interfacial intermetallic compounds (IMCs) in Sn-0.7Cu/Cu solder joint. The effect of sputtering parameter on the principal crystal orientation of Cu 6 Sn 5 coating was researched firstly, followed by the investigation on the influence of Cu 6 Sn 5 coating principal orientation on the interfacial IMCs growth kinetics. The influence mechanisms were studied using molecular dynamics simulations and first-principles calculations. The results revealed that the increasing sputtering power from 40 W to 60 W and 80 W can not only improve the bonding property between the prepared Cu 6 Sn 5 coating and Cu substrate, but also promote the transformation of the coating principal orientation from (132) to (132)/(22-1) and (132)/(22-1)/(42-2). Moreover, the three prepared Cu 6 Sn 5 coatings can inhibit IMC growth at SC07/Cu solder joint, and the Cu 6 Sn 5 coatings with (132)/(22-1) and (132)/(22-1)/(42-2) principal orientations exhibit more significant inhibitory effects on IMC growth than that with (132) principal orientation. It can be proved in this work that the growth of interfacial IMCs in Sn-0.7Cu/Cu solder joint at aging stage is mainly caused by the diffusion of Cu from Cu substrate toward Cu 6 Sn 5 phase. The difference in the growth behavior of IMCs can be attributed to the fact that when the Cu atoms diffuse across Cu 6 Sn 5 (22-1) and Cu 6 Sn 5 (42-2), the bonding strength between the Cu atom at the saddle point and its surrounding atoms is significantly larger than when diffusing across Cu 6 Sn 5 (132), leading to the smaller diffusion coefficients and a slower interfacial IMCs growth rate.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing