Abstract:Moisture absorption and dimensional distortion are the major drawbacks of wood utilization as building material. In this study, poplar wood coated with a thin layer of titanium dioxide (TiO2) was prepared by the cosolvent-controlled hydrothermal method. Subsequently, its moisture absorption and dimensional stability were examined. Scanning electron microscopy analysis revealed that the wood substrate was closely and entirely covered with the TiO2 coat. Microscale features were visible despite masking of the ultrastructural features of the cell wall. To explore the effects of TiO2 coating on the water-repellency and dimensional stability of wood, a 90-day water immersion test was carried out. Results showed that water absorption and thickness swelling of TiO2-coated wood increase very slowly and minimally. Weight change after 90 days of water immersion was reduced to 20.5%, nearly one-tenth of untreated control wood, and that maximum cross-sectional relative swelling was only 1.2%. Specimens were conditioned for 3 months at 20%, 30%, 40%, 50%, 60%, 70%, 80%, and 90% relative humidity (RH) to determine the effects of RH on moisture absorption and dimensional swelling of TiO2-coated wood. There was no change in weight after 3 months of being exposed to humidity conditions below 60%, whereas there was linear weight increase above 60% RH, but the maximum change was less than 6%. Cross-sectional relative swelling was less than 0.3% below 60% RH but increased as RH exceeded 60%. The maximum change was approximately 3%. Anisotropic thickness swelling of wood was almost eliminated after coating. It is obvious that TiO2 coating can act as a moisture barrier for wood and is an exceptionally strong water vapor-inhibiting shield under very humid conditions.

Ph-Dependent Structure and Wettability of TiO2-based Wood Surface

Controllable hydrothermal synthesis, optical and photocatalytic properties of TiO 2 nanostructures

Reversible Photocontrol of Wood-Surface Wettability Between Superhydrophilicity and Superhydrophobicity Based on A Tio2 Film

Growth of Hydrophobic Tio2 on Wood Surface Using A Hydrothermal Method

Fabrication of Modifier-Free Superhydrophobic Surfaces with Anti-Icing and Self-Cleaning Properties on Ti Substrate by Anodization Method

Tuning the Photoelectronic and Photocatalytic Properties of Single-Crystalline TiO 2 Nanosheet Array Films with Dominant {001} Facets by Controlling the Hydrochloric Acid Concentration

Natural Hydrophobicity and Reversible Wettability Conversion of Flat Anatase TiO₂ Thin Film.

Effect of Surface Morphology on Wettability Conversion

Hydrophobicity and Photocatalytic Activity of a Wood Surface Coated with a Fe3+-Doped SiO₂/TiO₂ Film

Surface Energy-Driven Solution Epitaxial Growth of Anatase TiO2 Homostructures for Overall Water Splitting

Degradation of formaldehyde and methylene blue using wood-templated biomimetic TiO2

Hydrophobic Modification of Bi2O3-Doped Si-Ti Composite Film on a Wood Surface

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Structure and reactivity of a water-covered anatase TiO<sub>2</sub>(001) surface

Preparation and characterization of TiO2 based on wood templates

Improvement of Water Resistance and Dimensional Stability of Wood Through Titanium Dioxide Coating

Organic Matter Transfer Caused by Concentration Difference Creates TC4 Surfaces with Switchable Wettability

Hydrophobic Modification of Wood Using Tetramethylcyclotetrasiloxane

Adsorption-Controlled Wettability and Self-Cleaning of TiO 2

Structure and Properties of Water on the Anatase Tio2(101) Surface: from Single-Molecule Adsorption to Interface Formation

Room Temperature Bilayer Water Structures on a Rutile TiO2(110) Surface: Hydrophobic or Hydrophilic?