Abstract:The zeolitic imidazolate frameworks (ZIFs) have been extensively investigated in adsorption, separation and catalysis for their unique properties, e.g., high surface area, ordered pore structures, tailorable frameworks and high chemical and thermal stability. Zn2+ and Co2+ are mostly used metal cations in ZIFs synthesis, because they prefer to form tetrahedron structures with imidazolates and their derived organic ligands. However the conventional preparation methods, which are generally performed at solvothermal condition in the sealed vessel, are time consuming and inhomogeneous process at micro-scale. As a result, the products are always different from batch to batch, which limits the scale-up of ZIFs by conventional synthesis methods. Therefore, facile ways to avoid these problems occurred in ZIFs synthesis are still needed to develop. The microfluidic system is of great advantages such as high surface to volume ratio, high mass and heat transfer efficiency and continuous flow processing. The continuous droplet microfluidic system is effective in mixing for the dynamic micro-environment inside droplets, and it is also effective in reducing the clogging problems for the confined synthesis of nanoparticles inside the microdroplets. Hence the droplet microfluidic system has been widely applied in nanomaterials synthesis. In this work, we design and fabricate a dual "T" type droplet microreactor to overcome the disadvantages of batch synthesis. The PDMS microchip was fabricated by a scaffold template assisting thermal curing process. Various ZIFs, including monoclinic C2/c ZIF-7, ZIF-8 and Co doped ZIF-8, were first synthesized in this microfluidic system to demonstrate a universal applicable synthesis method. The concentration of starting material and reaction time were studied in the synthesis of all ZIFs in this work. The results indicated that the increasing of concentration and retention time led to the increasing particles size in all ZIFs, as well as the increasing of product yield. However, the space-time yield was dramatically decreased while the retention time increased from 1 to 5 min, while the yield was just slightly increased. It was because that the micro-synthesis process had been significantly intensified in 1 min for the high mixing and diffusion efficiency in the microfluidic system. Moreover, the mixture solvent of methanol and ammonia water strongly facilitated the formation of ZIFs as well. The high throughput microfluidic system showed an estimated space-time yield of monoclinic C2/c ZIF-7 (461 kg/(cm3 d)), ZIF-8 (267 kg/(cm3 d)) and Co-ZIF-8 (160 kg/(cm3 d)) in a single microreactor, respectively. It paves the way to massively produce ZIFs without scale-up effect. All the ZIFs obtained from microreactions had high crystallinity except ZIF-67. ZIF-7 synthesized in these conditions showed a typical monoclinic C2/c ZIF-7 phase respect to the existence of water in the mixture solvents, which drove the structure from porous phase into the dense phase of monoclinic C2/c ZIF-7. ZIF-8 and Co-ZIF-8 both exhibited sodalite structure respect to the tetra coordination properties of Zn2+ and Co2+. The small polyhedron ZIF-8 particles had grown into large cubic particles with reaction time increased to 5 min. The Co doping exhibited strong effect on the particles morphology. The Co-ZIF-8 prepared from low concentration reactants showed spherical octadecahedron morphology, where {110} surfaces were the main surface. On the contrary, the high concentrated reactants resulted in cubic octadecahedron, where the {100} were mainly occupied the surface. The reason could be that the pure Co was difficult to form ZIF-67 in this condition; therefore the Co changes the formation of ZIF-8. Accordingly, this work provides a facile approach to massively produce diverse ZIFs with controllable morphology in microfluidic system.

Synthesis of zeolitic imidazolate framework nanocrystals

Vapor-assisted conversion synthesis of prototypical zeolitic imidazolate framework-8

Synthesis of millimeter-scale ZIF-8 single crystals and their reversible crystal structure changes

Controlled synthesis of hierarchical zeolitic imidazolate framework-GIS (ZIF-GIS) architectures

Zeta Potential and Size Analysis of Zeolitic Imidazolate Framework-8 Nanocrystals Prepared by Surfactant-Assisted Synthesis

Facile fabrication of nanoscale hierarchical porous zeolitic imidazolate frameworks for enhanced toluene adsorption capacity

Exceptional chemical and thermal stability of zeolitic imidazolate frameworks

Water-Based Synthesis Of Zeolitic Imidazolate Framework-8 With High Morphology Level At Room Temperature

High-yield synthesis of zeolitic imidazolate frameworks from stoichiometric metal and ligand precursor aqueous solutions at room temperature

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Synthesis of zeolitic imidazolate frameworks in droplet microfluidic system

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Surfactant‐Free, Size‐Controllable, and Scalable Green Synthesis of ZIF‐8 Particles with Narrow Size Distribution by Tuning Key Reaction Parameters in Water Solvent

A general and facile strategy for precisely controlling the crystal size of monodispersed metal-organic frameworks via separating the nucleation and growth.

Effect of altering linker ratio on nano-ZIF-8 polymorphisms in water-based and modulator-free synthesis

Systematic Study of Ionic Liquid Microemulsion Method for Nano-sized MOF, ZIF-8 Synthesis

Moisture-Assisted Synthesis and Carbon Dioxide Capture Performance of ZIF-L in Methanol Solution

Sol–Gel Synthesis of High‐Density Zeolitic Imidazolate Framework Monoliths via Ligand Assisted Methods: Exceptional Porosity, Hydrophobicity, and Applications in Vapor Adsorption

Formation of high crystalline ZIF-8 in an aqueous solution