Abstract:Monolithic ZIF‐8 and ZIF‐67 adsorbents are synthesized at room temperature using a novel, ligand‐assisted method. Despite reductions in crystallinity within some of the samples, monolithic zeolitic imidazolate frameworks (ZIFs) have superior volume‐relative microporosity, total porosity, and surface areas relative to their particulate counterparts due to increased density. Samples synthesized using a single modulator, n‐butylamine, have a hierarchical porosity resulting in improved adsorption capacities in mid‐ to high‐ sorbate pressure regions. ZIF‐67 monoliths produced through mixed‐modulator synthesis, n‐butylamine and 1‐methylimidazole, are almost entirely microporous. Vapor adsorption isotherms find that, whilst their amorphous content results in increased water uptake, monolithic ZIFs are found to possess higher surface and adsorption hydrophobicity than traditional non‐polar adsorbents. Cosorption measurements with a common VOC toluene, under humid conditions, find that these monolithic ZIF samples outperform powder equivalents, with the mixed‐modulator ZIF‐67 monolith capturing 28% more VOC compared to the powder ZIFs studied due to its superior volumetric efficiency. This study provides insights into the benefits of modulator‐based tuning of porosity within monolithic ZIFs which, combined with their hydrophobicity, may facilitate their application for industrial organic vapor recovery or indoor air cleaning, where efficient hydrophobic adsorbents which can operate in humid environments are essential.

Exceptional chemical and thermal stability of zeolitic imidazolate frameworks

Thermal and mechanical stability of zeolitic imidazolate frameworks polymorphs

Synthesis of millimeter-scale ZIF-8 single crystals and their reversible crystal structure changes

Design and synthesis of zeolitic tetrazolate-imidazolate frameworks

Controlled synthesis of hierarchical zeolitic imidazolate framework-GIS (ZIF-GIS) architectures

Sustainable Synthesis of Zeolitic Imidazolate Frameworks at Room Temperature in Water with Exact Zn/Linker Stoichiometry

Functionality-Induced Locking of Zeolitic Imidazolate Frameworks

Design and Generation of Extended Zeolitic Metal-Organic Frameworks (zmofs): Synthesis and Crystal Structures of Zinc(ii) Imidazolate Polymers with Zeolitic Topologies.

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Vapor-assisted conversion synthesis of prototypical zeolitic imidazolate framework-8

Data-Driven Search Algorithm for Discovery of Synthesizable Zeolitic Imidazolate Frameworks

Formation of high crystalline ZIF-8 in an aqueous solution

Specific Anion Effects on the Stability of Zeolitic Imidazolate Framework-8 in Aqueous Solution

High-yield synthesis of zeolitic imidazolate frameworks from stoichiometric metal and ligand precursor aqueous solutions at room temperature

An Experimental and Computational Study of Zeolitic Imidazole Framework (ZIF-8) Synthesis Modulated with Sodium Chloride and Its Interaction with CO2

Sol–Gel Synthesis of High‐Density Zeolitic Imidazolate Framework Monoliths via Ligand Assisted Methods: Exceptional Porosity, Hydrophobicity, and Applications in Vapor Adsorption

Uncovering Zeolitic Imidazolate Frameworks through Digitization of Chemical Insights

Facile fabrication of nanoscale hierarchical porous zeolitic imidazolate frameworks for enhanced toluene adsorption capacity

Water-Based Synthesis Of Zeolitic Imidazolate Framework-8 With High Morphology Level At Room Temperature

What makes zeolitic imidazolate frameworks hydrophobic or hydrophilic? The impact of geometry and functionalization on water adsorption

Overcoming the crystallization and designability issues in the ultrastable zirconium phosphonate framework system