Abstract:Wood delignification can provide a wood-based template with sufficient pore volume for polymer/wood composites. At the same time, delignification is conducive to the penetration of polymer into the wood cell wall, which is of great significance to improve the function and performance of composites. However, lignin is the main chemical component in wood. The removal of lignin will inevitably lead to the change of the wood's physical properties, including the hygroscopicity of the wood. In this study, prepolymerized methyl methacrylate (MMA) impregnated delignified wood (DW) was used to obtain polymerized methyl methacrylate/delignified wood (PMMA/DW) composites with different lignin removal. The effect of lignin removal on the hygroscopicity of the composites is discussed. The results of nitrogen adsorption showed that the DW could adsorb more nitrogen than the original wood, and the amount of nitrogen adsorption gradually increased with the improvement of the processing degree. After filling with PMMA, the adsorption amount of nitrogen was greatly reduced. The results of the BET analysis showed that delignification promoted the distribution of PMMA in the pores of the wood cell wall. When lignin was almost completely removed, all mesopores in the cell wall were filled with PMMA. The results of the moisture absorption analysis isotherm curve showed that the moisture absorption content of the wood was positively correlated with the amount of lignin removed, and the moisture absorption content of the PMMA/DW composite was negatively correlated with the amount of lignin removed. The hygroscopic data were further analyzed using the Hailwood–Horrobin model. The results showed that the mole number of adsorbable or hydratable sites of the DW increased with the increase of lignin removal, and the situation of the PMMA/DW composites was just the opposite. In addition, after delignification, the dissolved water content and hydrated water content of the DW increased, and the increase was related to the delignification strength. The increase of dissolved water content indicates that the removal of lignin promotes the production of more volume in the cell wall, which provides space for the adsorption of multilayer water. After MMA in situ polymerization, the hydration and dissolved water content of the PMMA/DW decreased significantly, and the dissolved water content decreased even more significantly. The fitting curves of the H-H model and GDW model for the experimental data points of the differently treated samples were similar. The removal of lignin led to the increase of the w value, indicating that the ratio of water molecules adsorbed in the first layer of DW to the second layer increased, and the removal of lignin resulted in the enhancement of wood hygroscopicity; the opposite was true for the PMMA/DW.

Fabrication and Mechanical Properties of Wood-Pmma Composite

Fabrication and properties of polypylene matrix composites reinforced by ultrafine bamboo-char

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Bulk Polymerization of PEGDA in Spruce Wood Using a DBD Plasma-Initiated Process to Improve the Flexural Strength of the Wood–Polymer Composite

Characteristics of paper mill sludge-wood fiber-high-density polyethylene composites

Fabrication and mechanism analysis of wood polymer composites with improved hydrophobicity, dimensional stability and mechanical strength

Effect of Lignin Removal on the Hygroscopicity of PMMA/Wood Composites

Fabrication and Characterization of PMMA/MWCNTs Composite Materials

Effect of wood flour and compatibilizer content on the properties of wood-plastic composites

Mechanical and Thermal Analysis of Poly (Vinyl-Alcohol) and Modified Wood Dust Composites

In Situ Construction of Thermotropic Shape Memory Polymer in Wood for Enhancing Its Dimensional Stability

Effects of Wood Content and Modification on Properties of Wood Flour/Polybutylene Adipate Terephthalate Biocomposites

Strong and Durable Wood Designed by Cell Wall Bulking Combined with Cell Lumen Filling

STRUCTURAL ASSESSMENT OF LAMINATED WOOD VENEER/PLASTIC SHEET COMPOSITES USED AS BUILDING MATERIAL

Effect of Chemical Modification on Mechanical Properties of Wood-Plastic Composite Injection-Molded Parts

Sustainable Engineering Polymer Composites Fabricated Using Delignified Bamboo Fiber as Reinforcement and Walnut Shell Powder as Filler

A novel thermoplastic material: Pre‐polymerized PMMA liquid resin and continuous glass fiber‐reinforced composite initiated by benzoyl peroxide/N,N‐dimethylaniline

Mechanical Properties and Flammability Analysis of Wood Fiber Filled Polylactic Acid (PLA) Composites Using Additive Manufacturing

Investigation of the Mechanical Properties of Poly(9,9-dioctylfluorene-alt-N-(4-sec-butylphenyl)-diphenylamine) (TFB)/wood/Polyethylene (PE) Composites

Investigate on the physical and mechanical properties of wood-polymer composition materials made on the premise of neighborhood wood flours

Research on the preparation and properties of foamed PP/wood flour composites