Abstract:A novel strong-base anion exchange fiber (QAPAN) was prepared in this study by preamination of a commercial poly(acrylonitrile) fiber followed by its subsequent grafting of glycidyl trimethylammonium chloride (GTA). The grafting conditions were optimized by conducting a L-18(3(7)) orthogonal test; and properties of the prepared QAPAN were investigated by multiple analyses. Results showed that the optimal reaction conditions were GTA dosage 4 mL, temperature 60 degrees C, reaction time 6 h, and volume ratio of water to dimethyl sulfoxide (DMSO) 0.5 : 0.5, among which volume ratio of water to DMSO was deemed as the most important factor on the QAPAN preparation. The prepared QAPAN had excellent fibrous morphology and fine mechanical stability, making its further processing feasible. Acid-base titration tests showed that the QAPAN had a total exchange capacity (TEC) of 6.34 mmol/g and a strong base capacity (SBC) of 1.34 mmol/g. Analyses of Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy further verified that the quaternary ammonium group was successfully grafted onto the QAPAN. This study provided a novel strong-base anion exchange fiber as well as a simple and repeatable method for its preparation. (C) 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 128:934-940, 2013

Preparation of Cation Exchange Fiber by Preradiation-Induced Grafting of Acrylic Acid Without Removal of the Inhibitor

Grafting Polymerization of Acrylic Acid Onto Preirradiated Polypropylene Fabric

Effect of Irradiation Grafting Epoxy on Surface Characteristics of Carbon Fibers and Mechanical Properties of Composites

Grafting copolymerization of N-isopropylacryamide onto preirradiated polypropylene fabric and Fe (II) adsorption

Surface modification of PVDF porous membranes by electron irradiation

Synthesis and Characterization of Cation-Exchange Fibers with Radiation-Induced Grafting of Glycidyl Methacrylate onto Cotton Cellulose

Grafting copolymerization of acrylamides onto preirradiated PP films

Preparation of Interpenetrating Polymer Networks by Two Times Grafting of Monomers Onto Preirradiated Polypropylene Film

Study on the Graft Reaction of Poly(propylene) Fiber with Acrylic Acid

STUDY ON PRE-IRRADIATION GRAFTING OF NIPAAm ONTO COTTON CELLULOSE FABRIC

Improved cationic dyeability of thermotropic liquid crystal polyarylate fabrics by ultraviolet irradiation-induced grafting of acrylic acid

Grafting copolymerization of N,N-dimethyacrylaminoethylmethacrylate (DMAEMA) onto preirradiated polypropylene films

Photo-Induced Graft Polymerization of Acrylamide on Polypropylene Membrane Surface in the Presence of Dibenzyl Trithiocarbonate

Grafting Copolymerization of Dimethylaminoethyl Methacrylate and Acrylic Acid Onto Preirradiated Polypropylene Film by Two-Step Reactions

Pre-irradiation Grafting Synthesis of Polystyrene-Divinylbenze Amidoxime Resin

Preparation of Temperature-Sensitive Polymer Films by Surface Photografting Techniques

Preparation and Characterization of A Novel Strong-Base Anion Exchange Fiber

Pre-irradiation Grafting of Temperature Sensitive Hydrogel on Cotton Cellulose Fabric

Study on Regularities of Graft Copolymerization of Acrylic Acid Onto Fungal Cell Wall

Preparation of New Hydrophilic PET Fiber by Grafting with Acrylic Acid and Modification with Amino Groups for Improvement of Dyeing Ability

GRAFT POLYMERIZATION OF AN OXAZOLIDINONYL-CONTAINING ACRYLIC MONOMER ON CELLULOSE FIBERS