Abstract:Traditional wood-polymer composite (WPC) based on the in situ polymerization of ethylene unsaturated monomers in the cellular cavity of wood is significant for the high-value-added utilization of low-quality wood. However, this type of WPC has the problems of volatile monomers, low conversion rates, odor residue, and poor compatibility between the polymer and wood interface, which hinder its promotion and application. In this study, a two-step process of cell wall bulking in combination with cell lumen filling was prepared to modify wood using Maleic anhydride (MAN) as the bulking agent and GMA-EGDMA (molar ratio 2:1) as the active monomer system. The results indicate that the modulus of rupture (MOR) (125.19 ± 8.41 MPa), compressive strength (116.38 ± 7.69 MPa), impact toughness (55.4 ± 2.95 KJ m-2), and hardness (6187 ± 273 N) of the bulking-filling wood composite materials were improved by 54%, 56%, 36%, and 66%, respectively, compared with those of poplar wood. These properties were superior to those of the traditional styrene (PSt)-WPC and even exceeded the performance of Xylosma congesta (Lour.) Merr, a high-quality wood from northeast China. Meanwhile, the mass loss of wood composite materials with bulking-filling treatment was only 2.35 ± 0.05%, and the internal structure remained intact, presenting excellent decay resistance. Additionally, the treatment also significantly improved the thermal and dimensional stability of the wood composites. This study provides a theoretical basis and guidance for realizing the high-value-added application of low-quality wood and the preparation of highly durable wood-based composites.

Wood-Polymer Composite Prepared by In Situ Synthesis of Copolymer within Wood and its Dimensional Stability

A Nanocomposite Structure Based on Modified MCM-48 and Polystyrene

Construction of Drug-Loaded Polyacrylate/Polyethylene Glycol Semi-Interpenetrating Network Structure in Wood and Its Performances

Wood-Based Nanocomposite Derived by in Situ Formation of Organic-Inorganic Hybrid Polymer within Wood via a Sol-Gel Method.

An effective technique for constructing wood composite with superior dimensional stability

Epoxy-Acrylic Polymer In-Situ Filling Cell Lumen and Bonding Cell Wall for Wood Reinforcement and Stabilization

In Situ Construction of Thermotropic Shape Memory Polymer in Wood for Enhancing Its Dimensional Stability

Strong and Durable Wood Designed by Cell Wall Bulking Combined with Cell Lumen Filling

Manufacturing and Characterization of Modified Wood with In Situ Polymerization and Cross-linking of Water-Soluble Monomers on Wood Cell Walls

Wood treatment using in situ polymerization of pine resin and styrene

Towards Low Polymer Content Transparent Composites Via Novel Integration Engineering

Fabrication and mechanism analysis of wood polymer composites with improved hydrophobicity, dimensional stability and mechanical strength

In situ fabrication of wood flour/nano silica hybrid and its application in polypropylene‐based wood‐plastic composites

Investigate on the physical and mechanical properties of wood-polymer composition materials made on the premise of neighborhood wood flours

Wood‐Derived Functional Polymeric Materials

Preparation and Closed-Loop Recycling of Ultra-High-Filled Wood Flour/Dynamic Polyurethane Composites

Preparation of Situ Microfiber-Reinforced Co-Extruded High-Filled Wood-Plastic Composite with Excellent Mechanical, Creep Resistance, and Water Resistance Properties

Effect of Polymer Blends on the Properties of Foamed Wood-Polymer Composites

Synthesis of biomass hyperbranched polyamide resin from cellulose and citric acid for wood adhesive

Preparation and characterization of micro/nanocellulose reinforced PVDF/wood composites

Enhanced Modification of Fast-Growing Wood: Application and Evaluation of Castor Oil-Based Unsaturated Polyester Resin