Abstract:Herein, we propose a new strategy to fabricate gold (Au) micro/nanostructure arrays by photocatalytic solid-state electrochemical reaction between superionic conductor RbAg4I5 and Au films. The Au and RbAg4I5 films were successively deposited on a clean quartz substrate by vacuum thermal deposition method. A copper microgrid possessing periodic holes 100 μm in diameter was put above the RbAg4I5 film as a mask plate, whereupon irradiation from a 405 nm wavelength laser was used to diffuse gold ions (Au+ ions) into vacant silver sites of RbAg4I5 and transfer Au+ through ion passageways in the RbAg4I5 film. When the laser was turned off, the Au+ ions were easily reduced due to low activity compared to the silver (Ag+) ions. After multiple on/off cycles of the 405 nm laser, the irradiated area of uniform Au film exhibited a periodic structural unit array whose period was the same as that of the mask plate hole array. Atomic force microscope and scanning electron microscope images revealed that a self-assembled needle-like nanostructure array grew perpendicular to the substrate surface inside each circle's structural unit. The height of the grown nanostructure array increased with laser power density. Raman enhancement of the gold nanostructure array as substrate was detected using Rhodamine 6G (R6G) ethanol solutions as probe molecules. The enhancement effect increased with the height of the grown nanostructure array, and could increase by two orders of magnitude greater than that of unirradiated Au film. This strategy offers a new method for the micro/nanostructure processing of gold and provides microscale-array-mediated surface-enhancement Raman-scattering (SERS) substrates comprising Au nanostructures for application in high-sensitivity spectrum analysis.

Self-Assembly of Gold Nanoparticle Arrays with Anodic Aluminum Oxide Template

Preparation of Nanochain and Nanosphere by Self-Assembly of Gold Nanoparticles

Synthesis and Optical Property of Gold Nanochains in the Biocompatible Solution System

Evaporation-Induced Self-Assembly of Gold Nanoparticles into A Highly Organized Two-Dimensional Array

Optical Device Based on a Nanopillar Array by the Pattern Transfer of an Anodic Aluminum Oxide Membrane

A Simple Method to Self-Assemble Two-dimensional and Three-dimensional Superlattices of Gold Nanoparticles

Assembly of Gold Nanoparticles into Aluminum Nanobowl Array

Arbitrary Gold Nanoparticle Arrays Fabricated Through AFM Nanoxerography and Interfacial Seeded Growth

Self-assembled gold micro/nanostructure arrays based on superionic conductor RbAg4I5 films

Gold Nanorods: Evaporative Self‐Assembly of Gold Nanorods into Macroscopic 3D Plasmonic Superlattice Arrays (adv. Mater. 13/2016)

Living Templates For The Merarchical Assembly Of Gold Nanoparticles

Evaporative Self‐Assembly of Gold Nanorods into Macroscopic 3D Plasmonic Superlattice Arrays

Fabrication of Oriented Arrays of Porous Gold Microsheaths Using Aligned Silver Nanowires As Sacrificial Template

Molecular Patterning and Directed Self-Assembly of Gold Nanoparticles on GaAs

Layered Assemblies of Single Crystal Gold Nanoplates: Direct Room Temperature Synthesis and Mechanistic Study

Layered Aggregates of Gold Nanoparticles: Solution and Surface-Assembled Structures

Hierarchical self-assembly of 1D and 2D ordered silver nanoparticle arrays on block copolymer templates

In situ self-assembly synthesis of gold nanoparticle arrays on polystyrene microspheres and their surface plasmon resonance

In-situ self-assembly growth of controllable gold nanoparticles film

Self-Assembly Of Gold Nanoparticle Chains Between Nanoelectrodes

Self-Assembly of Gold Nanoparticles on Nanometre-Patterned Surface