Self-Assembly of Gold Nanoparticles on Nanometre-Patterned Surface

YJ Zhang,JH Yang,W Li,Y Zhang,L Xu,J Xu,XF Huang,KJ Chen

DOI: https://doi.org/10.1088/0256-307x/22/12/042

2005-01-01

Abstract:The self-assembly processes of gold nanoparticles on nanometre-step-patterned Si surface and polished Si surface are investigated by the convective self-assembly method. The convective self-assembly method is used to deposit the colloids dispersed in benzene onto the substrates. The SEM results show that the configurations of the gold arrays depend on the surface morphology of the substrates. On the nanometre-step-patterned Si surface, the nanoparticles self assemble into parallel lines, and the distance between the neighbouring lines is around 35 nm. On the polished Si surface the nanoparticles form compact domains. In each domain the particles are close-packed in a two-dimensional hexagonal superlattice and are separated by uniform distances. The analysis shows that on the nanometre-step-patterned Si surface, the steps play critical roles in the self-assembly process of gold nanoparticles. The capillary force from the steps drives the particles to lines along the steps. Therefore, the particles tend to self-assemble into one-dimensional line structures when the solvent evaporates. For the polished Si substrate there is a little difference that the particles form two-dimensional hexagonal superlattices without the directional confinement.