Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Effects of Different Ions on the Corrosion Behavior of SM 80SS Tubing Steel in CO2/H2S Containing Aqueous Solution

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Effect of carbon dioxide on corrosion of tubular steel in high hydrogen sulfide and carbon dioxide environments

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

20 10 HIGH SALT CONCENTRATION EFFECTS ON CO 2 CORROSION AND H 2 S CORROSION

Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment

Effect of Service Environmental Parameters on Electrochemical Corrosion Behavior of L80 Casing Steel

Effect of temperature on electrochemical corrosion behavior of N80 and KO80SS steels in the stratum water with saturated CO2

CO2/H2S Corrosion Behavior of Tubular Steel N80 at Different H2S Partial Pressures

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

EIS Analysis on the Cathode Process of CO2/H2S Corrosion of Tubular Steel N80

Study on corrosion behavior of P110S steel in CO2-H2S- saturated solution

INFLUENCE OF SATURATED H_2S ON CORROSION BEHAVIOR OF 316L STAINLESS STEEL

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Unraveling the Impact of Cr Content on the Corrosion of Tubing Steel in High CO2 and Low H2S Environments

Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions

CORROSION PROPERTIES OF SPV50Q STEEL IN H2S-CONTAINING SOUR ENVIRONMENT

Effect of CO2/H2S and Applied Stress on Corrosion Behavior of 15cr Tubing in Oil Field Environment