Abstract:This study deals with doping of CeO2 with different cations M (M = Ti4+, Sn4+, Hf4+, Zr4+, La3+, Y3+ and Sm3+) to improve the reaction activity in two step thermochemical CO2 splitting reaction. The results show that the addition of tetravalent cations M (M = Ti4+, Sn4+, Hf4+ and Zr4+) into CeO2 significantly enhances the O-2 evolution activity. The O-2 production at 1400 degrees C increases as follows: CeO2 (2.5 ml/g) < Ce0.75Zr0.25O2, (6.5 ml/g) < Ce0.75Hf0.25O2 (7.2 ml/g) < Ce0.8Sn0.2O2 (11.2 ml/g) < Ce0.8Ti0.2O2 (13.2 ml/g). The corresponding CO production is increased from 4.5 ml/g for CeO2 up to 10.6 ml/g for Ce0.75Zr0.25O2 synthesized by solution combustion method. For Ce0.75Hf0.25O2 and Ce0.75Zr0.25O2 synthesized by hydrothermal method, steady-state CO and O-2 production with a ratio of near 2 occurs simultaneously when the temperature exceeds 1100 degrees C and we define the phenomena as "one step thermochemical CO2 splitting reaction". Further investigations for one step thermochemical CO2 splitting with both CeO2 and Ce0.75Zr0.25O2 as catalysts and blank reaction tube as reference from 1200 degrees C to 1400 degrees C are also performed. 16.8 ml/h of CO was produced for 0.5 g of Ce0.75Zr0.25O2 at 1400 degrees C which indicates that one step reaction may be a promising way for CO2 reduction. For Ce0.8Ti0.2O2 and Ce0.8Sn0.2O2, although the O-2 production is increased several times as compared to CeO2, the CO generation activity is still low due to the formation of Ce2Ti2O7 and Ce2Sn2O7 after the high temperature reduction reaction. The doping of trivalent cations M (M = La3+, Y3+ and Sm3+) into ceria has negative effect both on the O-2 evolution activity and the CO production. The estimated activation energy for the reduction step of Ce0.75Zr0.25O2 is much lower than that of CeO2 and Ce0.85La0.15O2-delta. The CO generation reaction of CeO2, Ce0.85La0.15O2-delta and Ce0.75Zr0.25O2-C (synthesized by solid solution combustion method) is a surface limited reaction. (C) 2013 Elsevier Ltd. All rights reserved.

Two-step Thermochemical Cycles for CO2 Splitting on Zr-doped Cobalt Ferrite Supported on Silica

Efficient CO 2 to CO Conversion at Moderate Temperatures Enabled by the Cobalt and Copper Co-Doped Ferrite Oxygen Carrier

Reactivity of Ni, Cr and Zr Doped Ceria in CO2 Splitting for CO Production Via Two-Step Thermochemical Cycle

Solar-driven Thermochemical Redox Cycles of ZrO2 Supported NiFe2O4 for CO2 Reduction into Chemical Energy

Copper and Cobalt Co-Doped Ferrites As Effective Agents for Chemical Looping CO2 Splitting

Two-step Thermochemical Looping Using Modified Ceria-Based Materials for Splitting CO 2

Enhanced Intermediate-Temperature CO2 Splitting Using Non-Stoichiometric Ceria and Ceria-Zirconia

Two-step thermochemical looping using modified ceria-based materials for splitting CO2

Enhancement Effects of Dopants and Sio2 Support on Mixed Metal Ferrites Based Two-Step Thermochemical Water Splitting

Thermochemical CO2 Splitting Reaction with Supported LaxA1−xFeyB1−yO3 (A = Sr, Ce, B = Co, Mn; 0 ⩽ X, Y ⩽ 1) Perovskite Oxides

Spinel-Structured Ternary Ferrites As Effective Agents for Chemical Looping CO2 Splitting

Platinum Group Metal Catalyst (RuOx, PtOx, and IrOx)-Decorated Ceria-Zirconia Solid Solution as High Active Oxygen Carriers for Solar Thermochemical CO2 Splitting

Platinum Group Metal Catalyst (RuO<sub><i>x</i></sub>, PtO<sub><i>x</i></sub>, and IrO<sub><i>x</i></sub>)-Decorated Ceria-Zirconia Solid Solution as High Active Oxygen Carriers for Solar Thermochemical CO<sub>2</sub> Splitting

Platinum Group Metal Catalyst (RuO x , PtO x , and IrO x )-Decorated Ceria-Zirconia Solid Solution as High Active Oxygen Carriers for Solar Thermochemical CO 2 Splitting

Self-assembly of a Highly Stable and Active Co3O4/H-TiO2 Bulk Heterojunction with High-Energy Interfacial Structures for Low Temperature CO Catalytic Oxidation

Copper ferrite and cobalt oxide two-layer coated macroporous SiC substrate for efficient CO2-splitting and thermochemical energy conversion

Cobalt-Based Perovskites as Efficient Oxygen Exchange Redox Materials for Solar Thermochemical Application

Thermochemical CO2 Splitting Reaction with CexM1−xO2−δ (M = Ti4+, Sn4+, Hf4+, Zr4+, La3+, Y3+ and Sm3+) Solid Solutions

Spinel Metal Oxide-Alkali Carbonate-Based, Low-Temperature Thermochemical Cycles for Water Splitting and CO2 Reduction

Thermochemical Activity of Single- and Dual-Phase Oxide Compounds Based on Ceria, Ferrites, and Perovskites for Two-Step Synthetic Fuel Production

Tuning the Support Properties Toward Higher CO2 Conversion During a Chemical Looping Scheme.