Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Single Crystallization of Olivine Lithium Phosphate Nanowires Using Oriented Attachments

Solution-phase synthesis of nickel phosphide single-crystalline nanowires

Realizing Single-Crystalline Vertically-Oriented and High-Density Electrospun Nanofibril Bundles by Controlled Postcalcination

Synthesis of Ultrafine Green-Emitting BaCO3 Nanowires with 18.5 Nm-Diameter by CO2 Vapor-Assisted Electrospinning

Array-orderly single crystalline silicon nano-wires

Oriented Nanofibers by a Newly Modified Electrospinning Method

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Synthesis of Triaxial Lifepo4 Nanowire with A Vgcf Core Column and A Carbon Shell Through the Electrospinning Method

One-Step, Catalyst-Free, Scalable in Situ Synthesis of Single-Crystal Aluminum Nanowires in Confined Graphene Space

A General Strategy to Electrospin Nanofibers with Ultrahigh Molecular Chain Orientation

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Progressively Oriented Attachment-Enabled Ultralong Single-Crystalline Upconversion Nanowires for Multidirectional Strain Sensing

Ultra‐Long Single‐Crystalline Α‐si3n4nanowires: Derived from a Polymeric Precursor

Fabrication of self-supported patterns of aligned beta-FeOOH nanowires by a low-temperature solution reaction.

Oriented Crystal Growth of Li0.33La0.557TiO3 Nanowire Induced by One-Dimensional Polymer Sheath toward Rapid Lithium-Ion Transfer

Synthesis of LiNi0.5Mn1.5O4 and 0.5li2mno3–0.5lini1/3co1/3mn1/3o2 Hollow Nanowires by Electrospinning

Single Crystalline SnO2 Nanowires Obtained from Heat-Treated SnO2 and C Mixture and Their Electrochemical Properties

Nanostructured LiCoO2 and LiMn2O4 fibers fabricated by a high frequency electrospinning

Preparation of Nanowire Arrays of Amorphous Carbon Nanotube-Coated Single Crystal SnO<sub>2</sub>

Oriented Crystal Growth of Li 0.33 La 0.557 TiO 3 Nanowire Induced by One-Dimensional Polymer Sheath toward Rapid Lithium-Ion Transfer