Fabrication and Evaluation of Light-Curing Nanocomposite Resins Filled with Surface-Modified TiO2 Nanoparticles for Dental Application

Miao Wu,Feimin Zhang,Jiahui Yu,Hongye Zhou,Di Zhang,Chong Hu,Jin Huang

DOI: https://doi.org/10.1007/s13726-014-0246-7

IF: 2.485

2014-01-01

Iranian Polymer Journal

Abstract:A kind of light-curing nanocomposite resin, which consisted of reactive monomers, surface-modified TiO 2 nanoparticles and a photoinitiation system, has been developed for the application of dental restoration. It may be noted that the conjugation of glycidyl methylmethacrylate (GMA) onto the surface of TiO 2 nanoparticles (nano-TiO 2 ) contributed to improvement in miscibility between nano-filler and matrix, because the reactive C=C group of GMA participated in curing of the matrix, and hence resulted in the enhancement of mechanical properties. When the content of GMA-modified nano-TiO 2 was 2 wt%, the flexural strength and modulus of the nanocomposite resin reached 147.8 and 2918.3 MPa, respectively, which increased by 21.7 and 30.8 % in contrast to the resin without adding nano-filler. Furthermore, the polymerization shrinkage decreased after incorporating the nano-filler while the degree of monomer conversion and the water sorption for the nanocomposite resins was comparable with those of the resin without nano-filler. In conclusion, this study presented a new method, namely introduction of functional groups onto the nano-filler surface to participate in the reaction of resin monomer, to improve the interfacial adhesion and the resultant miscibility between nano-filler and resin matrix in light-curing dental nanocomposites by chemical linkage mediated with surface-modified specie. Moreover, the enhanced mechanical properties and decreased polymerization shrinkage of nanocomposite resins, which are considered the key to the effects of dental restoration, contributed a great potential as a dental material utilized for caries treatment and prevention.