Abstract:Purpose: Mechanical properties of dental composite resins need to be improved in order to enhance their performance for applications in direct restorations. Application of nanoparticles in this field is a recent development. The aim of this study was to investigate the mechanical properties of experimental composites containing various mass fractions of silica nanoparticles. Materials and methods: Experimental composites were composed of a visible-light-curing monomer mixture (70 wt% Bis-GMA and 30 wt% TEGDMA) and silica nanoparticles of a size ranging from 20 nm to 50 nm modified with gamma-methacryloxy propyl trimethoxy silane (gamma-MPS) as reinforcing filler. The composites were classified into four groups according to their filler mass fractions ranging from 20% to 50%. Following the same preparation procedure, a conventional composite was also fabricated consisting of a mass percentage of 60% silica fillers having particle sizes ranging from 10 microm to 40 microm in the same organic matrix, which served as control. Ten specimens were prepared of each experimental group and also of the control. Fracture toughness was measured using single-edge notched bend (SENB) specimens. Specimen fracture surfaces were mounted on aluminum stubs with carbon cement, sputter-coated with gold and examined under scanning electron microscopy (SEM). Flexural strength was evaluated through a standard three-point bending test and Vickers microhardness test was performed to investigate the hardness of the samples. Results: Filler mass fraction had a significant effect on composite properties. Fracture toughness, flexural strength, and hardness of composites at filler mass fraction of 40% of silica nanoparticles were (mean +/- SD) 1.43 +/- 0.08 MPa.m(1/2), 149.74 +/- 8.14 MPa, and 62.12 +/- 3.07 VHN, respectively; relevant values for composites at 50% mass fraction of silica nanoparticles were 1.38 +/- 0.07 MPa.m(1/2), 122.83 +/- 6.13 MPa, and 70.69 +/- 3.67 VHN, respectively, all of which were significantly higher than 1.07 +/- 0.06 MPa.m(1/2), 104.61 +/- 8.73 MPa, and 52.14 +/- 4.02 VHN of the control, respectively (Tukey's multiple comparison test; family confidence coefficient = 0.95). Measured values for composites at 20% mass fraction of silica nanoparticles were 0.94 +/- 0.06 MPa.m(1/2), 103.41 +/- 7.62 MPa, and 42.87 +/- 2.61 VHN, respectively; relevant values for composites at 30% mass fraction of silica nanoparticles were 1.16 +/- 0.07 MPa.m(1/2), 127.91 +/- 7.05 MPa, and 51.78 +/- 3.41 VHN, respectively. Conclusions: Reinforcement of dental composite resins with silica nanoparticles resulted in a significant increase in the evaluated mechanical properties in comparison with the conventional composite. The filler mass fraction played a critical role in determining the composite's mechanical properties.

Nanoparticle-reinforced Resin-Based Dental Composites.

Microstructure and Mechanical Properties of Nano-Tio2 Reinforced Dental Composite Resin

Fabrication and Evaluation of Light-Curing Nanocomposite Resins Filled with Surface-Modified TiO2 Nanoparticles for Dental Application

[Surface Modification and Microstructure of Single-Walled Carbon Nanotubes for Dental Composite Resin].

Study on Micro-Structure of the Nano Enforced Dental Composite Resin

Effect of Nano SiO 2 Particles on the Morphology and Mechanical Properties of POSS Nanocomposite Dental Resins

Effect of Silica Nanospheres Silanized by Functional Silanes on the Physicochemical and Mechanical Properties of Bis-GMA/TEGDMA Dental Composite Resin by Photocuring Synthesis

Effects of Three Different Nanometer Particles on Mechanical Properties of Dental FRC Posts Matrix Resin

Preparation and Properties of Nano-SiO2/TDE-85/BMI/BADCy Composites

Investigation of mechanical properties of experimental Bis-GMA/TEGDMA dental composite resins containing various mass fractions of silica nanoparticles

Improved performance of Bis-GMA/TEGDMA dental composites by net-like structures formed from SiO2 nanofiber fillers

Physical and Mechanical Properties of Dental Nanocomposites Composed of Aliphatic Epoxy Resin and Epoxidized Aromatic Hyperbranched Polymers

Nanoindentation Study on Mechanical Properties and Curing Depth of Dental Resin Nanocomposites

[Mechanical and light-activated antibacterial properties of resin filled with Ag-TiO2 nanoparticles].

Evaluation of Micro-Tensile Bond Strength of Fibre Post with Titanium Dioxide Nanoparticles as Fillers in Experimental Dental Composite Resin

Improved performance of Bis-GMA/TEGDMA dental composites by net-like structures formed from SiO 2 nanofiber fillers

The researchment of nami-material reinfoced dental composite resin

Titanium dioxide nanotubes with triazine-methacrylate monomer to improve physicochemical and biological properties of adhesives

Synthesis of polymethyl methacrylate/depolymerized polyethylene terephthalate blend reinforced by titanium dioxide nanoparticles for dental fillings applications

Nanoindentation Study on Mechanical Properties of Nano-SiO2/Dental Resin Composites

Effects of Titanium Dioxide Nanoparticles on the Mechanical Strength of Epoxy Hybrid Composite Materials Reinforced with Unidirectional Carbon and Glass Fibers.