Abstract:A series of Cu/SAPO-34 catalysts of identical chemical compositions but different crystallite sizes (1-13 mu m) was prepared by "one-pot" method. The fresh and low-temperature hydrothermally treated (LHT) catalysts were characterized by a comprehensive set of techniques, including XRF, SEM, EDS, XRD, NMR, BET, XPS, pyridine-FTIR, NH3 and diethylamine TPD, EPR as well as H-2-TPR. The reaction rates for NH3-SCR were measured under differential conditions and correlated with their physical and chemical properties. All fresh catalysts, regardless of crystallite size, showed the same bulk properties, such as chemical composition, crystallinity, acidity and copper species. After a hydrothermal treatment (96 h at 70 degrees C with 80% humidity), loss of micropore surface area, micro volume, relative crystallinities, acidity and isolated Cu2+ species was observed on all catalysts, and the extent of decrease was proportional to the average crystallite size. NH3-SCR reaction rate suffered a similar decrease with increasing crystallite size. Surface analyses by SEM-ESD, XPS and diethylamine-TPD showed an obvious surface enrichment of Si (and Bronsted acidity) on all fresh catalysts, and the degree of enrichment is also proportional to crystallite size. This surface enrichment of Si-O-Al linkages is thought to be the root cause for the structural vulnerability found on larger crystallite catalysts under LHT conditions. This understanding is entirely consistent with the observation found on the H/SAPO-34 reference materials of the same sizes, where the structural destruction is even more severe after the LHT. A mechanism for structural disintegration for larger Cu/SAPO-34 crystals was proposed, and the genesis of the Si gradient was discussed in the context of crystallization kinetics.

Improvement of Low-Temperature Hydrothermal Stability of Cu/Sapo-34 Catalysts by Cu2+ Species

Insights into the Effects of Sulfate Species on CuO/TiO2 Catalysts for NH3-SCR Reactions

Evolution of Copper Species on Cu/SAPO-34 SCR Catalysts Upon Hydrothermal Aging

A controllable zeolite framework stability of Cu/SAPO-34 via adjusting the copper coordination environment for NH 3 -SCR under hydrothermal condition

The Migration of Cu Species over Cu–SAPO-34 and Its Effect on NH3 Oxidation at High Temperature

The Influence of Crystallite Size on the Structural Stability of Cu/SAPO-34 Catalysts

Improved hydrothermal stability of Cu-SSZ-13 by SAPO-34 modification: Framework stability and inter-particle migration

New Insight into Cu/SAPO-34 Preparation Procedure: Impact of NH4-SAPO-34 on the Structure and Cu Distribution in Cu-SAPO-34 NH3-SCR Catalysts

Boosting the Catalytic Performance of Cu-SAPO-34 in NOx Removal Via Hydrothermal Treatment.

Critical Roles of Cu(OH)2 in Low-Temperature Moisture-Induced Degradation of Cu-SAPO-34 SCR Catalyst: Correlating Reversible and Irreversible Deactivation

Promotional effect of ion-exchanged K on the low-temperature hydrothermal stability of Cu/SAPO-34 and its synergic application with Fe/Beta catalysts

The effect of Si environments on NH3 selective catalytic reduction performance and moisture stability of Cu-SAPO-34 catalysts

Understanding the direct relationship between various structure-directing agents and low-temperature hydrothermal durability over Cu-SAPO-34 during the NH 3 -SCR reaction

Migration of Cu Species in Cu/SAPO-34 During Hydrothermal Aging

Destructive and Protective Effects of NH3 on the Low-Temperature Hydrothermal Stability of SAPO-34 and Cu-SAPO-34.

Hydrothermal tolerance towards different temperature conditions over two typical Cu/CHA catalysts

Boosting the catalytic performance of Cu-SAPO-34 in NO removal via hydrothermal treatment

Unravelling the Phosphorus-Induced Effect on NH3-SCR Catalytic Performance, Hydrothermal Stability and SO2 Resistance of Cu/SAPO-34

Migration, Reactivity, and Sulfur Tolerance of Copper Species in SAPO-34 Zeolite Toward NOx Reduction with Ammonia

Unraveling the Nature of Cerium on Stabilizing Cu/SAPO-34 NH3-SCR Catalysts under Hydrothermal Aging at Low Temperatures

Enhanced hydrothermal stability of Cu-SSZ-13 by compositing with Cu-SAPO-34 in selective catalytic reduction of nitrogen oxides with ammonia