Abstract:We report here a generalized synthesis of various crystalline mesoporous metal oxides including CeO2, Cr2O3, Fe2O3, SnO2, Ce0.5Zr0.5O2, TiO2, Al2O3 and ZrO2 from the self-assembly of a basic poly 4-vinylpyridine (P4VP) template with various metal precursors based on their strong acid–base interaction under high temperature (180 °C) hydrothermal conditions. Using the typically crystalline mesoporous metal oxide of CeO2, after removing the template by calcination at 550 °C and loading with various transition metal oxides such as MnOx, various transition metal oxide functionalized crystalline mesoporous CeO2 (MnOx/P4VP–CeO2) were obtained. X-ray diffraction (XRD) patterns show that the resulting mesoporous metal oxides exhibit a high degree of crystallinity, and the transition metal oxides active sites have been successfully loaded into these samples. N2 sorption–desorption isotherms, SEM images show that the resulting crystalline mesoporous metal oxides, such as CeO2, have a large BET surface area (94 m2 g−1) and abundant mesopores, which exhibit monolithic morphology with crystal sizes ranging from 5 to 15 μm, giving a uniform pore size centered at 5 nm. XPS spectra show that the active sites such as MnOx exhibit the phases of MnO2 and Mn2O3 in P4VP–CeO2. H2-TPR curves show that MnOx/P4VP–CeO2 exhibits decreased reductive temperatures of both active sites of the MnOx and P4VP–CeO2 supporter when compared with the samples reported previously. More importantly, MnOx/P4VP–CeO2 exhibits much better catalytic activities and good recyclability for catalyzing the oxidation of benzene than that of MnOx loaded commercially crystalline CeO2, which will be very important for their wide applications for VOCs removal in industry.

Adsorption/desorption and catalytic oxidation of VOCs on montmorillonite and pillared clays

Synthesis and Characterization of Aluminum and Al/REE Pillared Clays and Supported Palladium Catalysts for Benzene Oxidation

Catalytic Performance of Pillared Interlayered Clays (pilcs) Supported CrCe Catalysts for Deep Oxidation of Nitrogen-Containing VOCs

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Preparation, Characterization and Catalytic Properties of Yttrium-Zirconium-Pillared Montmorillonite and Their Application in Supported Ce Catalysts

Effects of Properties of Minerals Adsorbents for the Adsorption and Desorption of Volatile Organic Compounds (VOC)

Pillared Clay-Supported Noble Metal And Metal Oxide Catalysts For Complete Oxidation Of Vocs

Hierarchical Zeolite Enveloping Pd-CeO2 Nanowires: an Efficient Adsorption/catalysis Bifunctional Catalyst for Low Temperature Propane Total Degradation

In-situ Synthesis of Monolithic Cu-Mn-Ce/cordierite Catalysts Towards VOCs Combustion

Porous Materials Engineering for Aromatic VOCs Combustion & Adsorption

Influence of synthesis condition on pore structure of Al pillared clays and supported Pd catalysts for deep oxidation of benzene

Catalytic Performance Of Pd Catalyst Supported On Zirconium And Yttrium Pillared Montmorillonite

The catalytic combustion of VOCs over copper catalysts supported on cerium-modified and zirconium-pillared montmorillonite

Effects of Clay Pore Structure and Addition of Cerium on Adsorption/Desorption and Catalytic Oxidation of Benzene

Catalytic oxidation of VOCs over 3D@2D Pd/CoMn2O4 nanosheets supported on hollow Al2O3 microspheres

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Adsorption of Volatile Organic Compounds Onto Natural Porous Minerals.

Facile and Flexible Preparation of Highly Active CuCe Monolithic Catalysts for VOCs Combustion

Adsorptive and Catalytic Properties in the Removal of Volatile Organic Compounds over Zeolite-Based Materials

Promoting effect of Ce added to metal oxide supported on Al pillared clays for deep benzene oxidation

Modification of Pillared Intercalated Montmorillonite Clay as Heterogeneous Pd Catalyst Supports