Catalytic Performance Of Pd Catalyst Supported On Zirconium And Yttrium Pillared Montmorillonite

QI Ling-Yan,Min Chen,Cui Song,ZHOU Ren-Xian,ZHENG Xiao-Ming

DOI: https://doi.org/10.3321/j.issn:1001-4861.2008.03.020

2008-01-01

Chinese journal of inorganic chemistry

Abstract:A montmorillonite support material pillared with zirconium and yttrium (Zr-Y-MMT) was prepared for catalytic oxidation of acetone, toluene and ethyl acetate. The Zr-Y-MMT support and the supported Pd catalyst (Pd/Zr-Y-MMT) were characterized by XRD, TEM and low temperature nitrogen adsorption-desorption techniques. The XRD results indicate that the interlayer spacing of the montmorillonite is increased from 1.27 nm to 1.78 nm after zirconium and yttrium cation pillaring. N-2 adsorption-desorption results show that a great increase in BET specific surface area (from 62 to 395 m(2).g(-1)) is found for Na-MMT pillared with zirconium and yttrium. It is also found that Zr-Y-MMT is more active than Na-MMT for the complete oxidation of acetone, toluene and ethyl acetate, and the temperature for the said catalytic oxidation can be lowered to 320 degrees C, 350 degrees C and 290 degrees C, respectively. Moreover, after 0.1wt% Pd was supported on Zr-Y-MMT, the catalytic activity was obviously improved for toluene combustion.