Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Mn x Co 3 − x O 4 solid solution as high-efficient catalysts for low-temperature oxidation of formaldehyde

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

NaBH4 reduced Mn-doped cobalt tetroxide R-MnxCo3-xO4 catalysts with plentiful oxygen vacancies for HCHO oxidation at low temperature

ZIF-67 Derived Cu-Co Mixed Oxides for Efficient Catalytic Oxidation of Formaldehyde at Low-Temperature

Mesoporous MnCeOx Solid Solutions for Low Temperature and Selective Oxidation of Hydrocarbons.

Synergistic effect of photo-thermal oxidation for a low concentration of HCHO over Bi3+-TiO2/MnFeOx catalysts at ambient temperature

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

Mn/HZSM-5 catalyst with high content of Mn 4+ and surface hydroxyls for formaldehyde oxidation at room temperature

High Surface Area Au/CeO2 Catalysts for Low Temperature Formaldehyde Oxidation

Two-step hydrothermal synthesis of highly active MnOx-CeO2 for complete oxidation of formaldehyde

Surface Lattice Oxygen Activation by Nitrogen-Doped Manganese Dioxide as an Effective and Longevous Catalyst for Indoor HCHO Decomposition

The Catalytic and Adsorptive Synergistic Effect of Oxygen-Vacancy-Rich MnO x /C Catalysts for HCHO Oxidation at Room Temperature

Formaldehyde oxidation at room temperature over layered MnO2

Sepiolite-Supported Manganese Oxide as an Efficient Catalyst for Formaldehyde Oxidation: Performance and Mechanism

Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature

Oxygen vacancy-rich K-Mn3O4@CeO2 catalyst for efficient oxidation degradation of formaldehyde at near room temperature

Transition metal-doped modification of lattice defects in formaldehyde catalysts − Controlling the specific surface area and mass transfer

Preparation of Mn-Fe Oxide by a Hydrolysis-Driven Redox Method and Its Application in Formaldehyde Oxidation

Oxygen vacancy–engineered δ-MnO /activated carbon for room-temperature catalytic oxidation of formaldehyde

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species