Abstract:A variety of core-shell structure catalysts with different shell thicknesses were fabricated by hydrothermal coating. Multiple characterization technologies including XRD, SEM, N2 adsorption-desorption, NH3-TPD and IR were employed to explore the physicochemical properties of all the samples, demonstrating that the shell layer was successfully introduced on the exterior of the core. The results of hexane cracking disclosed that with the increase of shell thickness, olefins selectivities increased continuously accompanied by a minor decrease of hexane conversion. Only when controlling the shell thickness to 150 nm could manifest the best performance with light olefins yields of 51.1 %, much higher than those of 23.2 % on the core catalyst. On the other hand, the catalyst lifetime was greatly improved, which presented a decrease of only 2.8 % in hexane conversion, relative to 9.7 % on the core catalyst during the reaction period of 80 h. Above exciting phenomenon was attributed to the growth of protective shell outside the core, which passivated the external acid sites greatly, thus side reactions were inhibited dramatically. It is firmly believed that our work provided a novel reference for the production of light oil cracking catalyst in industry, which will make up for the shortage of olefins considerably. Core-shell structure catalysts fabricated demonstrated a volcanic trend in olefins yields with the increase of shell thickness. Controlling shell thickness to 150 nm could manifest the best performance with 27.9 % higher in olefins yields and dramatically improved catalyst lifetime compared with the core catalyst ascribed to passivation of external acid sites by protective shell outside the core to inhibit side reactions considerably.image

Characterization and application of a Pt/ZSM-5/SSMF catalyst for hydrocracking of paraffin wax

ZSM-5 Crystals Grown on the Wall of a Long Tubular Reactor As a Structured Catalyst for Cracking of Endothermic Fuels

ZSM–5@KIT–6 encapsulated composite molecular sieves for the catalytic cracking of waste cooking oil model compound to produce light olefins

Heat Transfer Study on Hydrocracking of Paraffin Wax over Microfiber-Wrapped Catalyst

Additional Β Zeolites in SiO 2 −al 2 O 3 Supported Pt and Pd Catalysts for Hydrocracking of Paraffin Wax

Effect of Different Ligands on the Preparation of Pt-xMn@HZSM-5 and Their Catalytic Performance for Iso-Butane Catalytic Cracking

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Hydrocracking of Bio-Alkanes over Pt/Al-MCM-41 Mesoporous Molecular Sieves for Bio-Jet Fuel Production

Hydrocracking and Hydroisomerization of N -Hexadecane, N -Octacosane and Fischer–Tropsch Wax over a Pt/SiO 2 –al 2 O 3 Catalyst

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of n-Decane

Preparation and characterization of NiW-nHA composite catalyst for hydrocracking.

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of <i>n</i>-Decane

Supported CoW Bifunctional Catalyst with High Activity and Selectivity for Hydrocracking Alkane

Hydrocracking diversity in n-dodecane isomerization on Pt/ZSM-22 and Pt/ZSM-23 catalysts and their catalytic performance for hydrodewaxing of lube base oil

SO 4 2− /tio 2 Promotion on HZSM-5 for Catalytic Cracking of Paraffin

The Effect of Additional Zeolites in Amorphous Silica–Alumina Supports on Hydrocracking of Semirefined Paraffinic Wax

Mechanistic Aspects of N-Paraffins Hydrocracking: Influence of Zeolite Morphology and Acidity of Pd(Pt)/ZSM-5 Catalysts

Fabrication and Characterization of ZSM‐5@Silicalite‐1 Core‐shell Composites and Their Application in Hexane Catalytic Cracking

Core-shell-structured Composite ZSM-5@MCM-41 Catalysts: Fabrication, Characterization, and Enhanced Performance in Hexane Catalytic Cracking

Hierarchical ZSM-5 zeolite designed by combining desilication and dealumination with related study of n-heptane cracking performance