Manipulation of ferromagnetic ordering in magnetic semiconductor Li 1.05 (Zn 0.925 ,Mn 0.075 ) As by In doping
Xie Ling-Feng,Dong Jin-Ou,Zhao Xue-Qin,Yang Qiao-Lin,Ning Fan-Long
DOI: https://doi.org/10.7498/aps.73.20231949
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:Magnetic semiconductors (MSs) that can manipulate both spin and charge degrees of freedom have become an important research field in semiconductor spintronics. In recent years, some new series of bulk form MSs, that are iso-structure to the iron-based superconductors were reported. In these new materials, spins and carriers are separately introduced, which enable it to be precisely manipulated. Li(Zn,Mn)As with T C ~50K is the first bulk MS with spins and charges separation. The carriers of Li(Zn,Mn)As is p -type, which is in contradiction with the theoretical calculation results by Mašek et al where they believe that doping extra Li will induce n -type carriers. However, it is still necessary to study the formation reason of hole carriers in Li(Zn,Mn)As and its effect on ferromagnetic ordering. In this paper, a series of Li 1.05 (Zn 0.925- y ,Mn 0.075 ,In y )As ( y =0, 0.05, 0.075, 0.1) new materials have been successfully synthesized by introducing n -type carriers into the p -type bulk MS Li 1.05 (Zn 0.925 ,Mn 0.075 )As through (Zn 2+ ,In 3+ ) substitution. Magnetization measurements reveal that all the samples still maintain a ferromagnetic transition signal similar to MS Li 1.05 (Zn 0.925 ,Mn 0.075 )As, and the Curie temperature T C is obviously suppressed with the increase of In-doping concentration. Clear hysteresis loops demonstrate the ferromagnetic ordering state. The resistivity increases gradually with the increase of In-doping concentration. Our results show that the (Zn 2+ , In 3+ ) substitution successfully introduces n-type carriers in Li 1.05 (Zn 0.925 ,Mn 0.075 )As, and the original p -type carriers in Li 1.05 (Zn 0.925 ,Mn 0.075 )As are partial neutralized, resulting in the decreasing of p -type carrier concentrations, which obviously suppressed the ferromagnetic ordering of Li(Zn,Mn)As. It reflects the important roles played by carriers in the formation of ferromagnetic ordering in MS materials. The fabrication of Li 1.05 (Zn 0.925- y ,Mn 0.075 ,In y )As material gives us a better understanding of the mechanism of ferromagnetic ordering in Li(Zn,Mn)As, and these results will be helpful for searching more novel magnetic semiconductor materials.
physics, multidisciplinary