Modified microstructures in proton irradiated dual phase 308L weldment filler material
Zhen Li,Xun Zhan,Xian-Ming Bai,Shao-Chun Lee,Weicheng Zhong,Benjamin J. Sutton,Brent J. Heuser
DOI: https://doi.org/10.1016/j.jnucmat.2021.152825
IF: 3.555
2021-05-01
Journal of Nuclear Materials
Abstract:<p>The effect of proton irradiation on the microstructure of δ ferrite—γ austenite mixed phase 308L filler material in a 508-304 dissimilar metal weldment was investigated over a depth of 0 to 10 µm. Ni-Si-Mn G-phase precipitates were observed with SEM and TEM in δ ferrite but not in γ austenite. Our density functional theory based calculations show that the G/Fe interface energy in δ-Fe is significantly lower than that in γ-Fe (0.35 versus 1.25 J/m<sup>2</sup>), which provides a thermodynamics-based explanation for our experimental observations of preferential formation of G-phase in δ ferrite. STEM-EDS, TEM dark field imaging, and diffraction patterns confirmed the Ni-Si-Mn enriched precipitates were G-phase precipitates with a stoichiometry of Mn<sub>6</sub>Ni<sub>16</sub>Si<sub>7</sub>. Intragranular voids and Ni-Si enriched clusters were observed in irradiated γ austenite. Additionally, Ni and Si segregation was observed along the void interfaces. In both cases, Ni-Si clusters and segregation to voids, selected area diffraction patterns did not reveal the existence of a second phase. Proton irradiation induced Cr depletion and Si and Ni enrichment at γ−γ austenite grain boundaries that was characterized with STEM/EDS.</p>
materials science, multidisciplinary,nuclear science & technology