Co-evolution of M 23 C 6 Precipitates and Cavities in a Boron-Free Ni-based Alloy GH3617 under High-Temperature He Ion Irradiation: Effects on Cavity Swelling and Mechanical Properties
Peng Jin,LinQi Zhang,MingHuan Cui,Jing Li,YuShan Yang,ZeYuan Chen,YiQiHui Lan,Chao Liu,ZhiWei Ma,JianLong Chai,YaBin Zhu,LanZhang Zhou,ZhiGuang Wang,TieLong Shen
DOI: https://doi.org/10.1016/j.matchar.2024.114437
IF: 4.537
2024-01-01
Materials Characterization
Abstract:Ni-based alloys are promising materials for advanced nuclear reactors operating at high temperatures due to their exceptional resistance to high temperatures and corrosion. Understanding the synergy of phase stability and helium effects is crucial for assessing the long-term performance and reliability of these alloys in advanced nuclear reactors. This study has investigated the co-evolution behavior of M 23 C 6 precipitates and cavities in a boron-free solid solution strengthened Ni-based alloy GH3617 under high-temperature He ion irradiation, and its impact on alloy swelling and mechanical properties, by He ion irradiation experiments with the highest fluence of 1 x 1017 17 He/cm2 2 up to 800 degrees C. Transmission Electron Microscopy (TEM) and Nanoindentation are employed to investigate microstructural evolution and mechanical properties, respectively. The findings show that at room temperature and 500 degrees C, cavities and dislocation loops were the dominant irradiation defects, whereas at 800 degrees C, the density of cavities and dislocations reduced while the formation of M 23 C 6 precipitates increased. These precipitates act as effective trapping sites for He and point defect, leading to cavity formation at the interfaces or within the precipitates. Moreover, increased irradiation fluence accelerates the co-evolution process, resulting in an increase in the density and size of both precipitates and cavities, ultimately leading to enhanced swelling. The {111} planes are favored interfaces between intragranular M 23 C 6 precipitates and the matrix due to their minimal misfit, while the preferred interface planes between cavities with octahedral or cubo-octahedral shapes and the precipitate/matrix are also {111}, owing to their lower surface energy as well. The co-evolution of cavities and precipitates was found to influence mechanical properties, resulting in an irradiation hardening effect at lower fluences, while softening at higher fluences. This study provides novel insights into the degradation mechanisms of Ni-based alloys under coupling effect of He and high-temperature irradiation.