Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Electrochemical characteristics of the early corrosion stages of API X52 steel exposed to H 2 S environments

Effect of Temperature and H<sub>2</sub>S Concentration on Corrosion of X52 Pipeline Steel in Acidic Solutions

Dependence of the Abnormal Protective Property on the Corrosion Product Film Formed on H2S-adjacent API-X52 Pipeline Steel

STUDY ON CORROSION AND INHIBITION MECHANISM IN H2S AQUEOUS SOLUTIONS Ⅱ.Passivity and Passive film Breakdown of Carbon Steel under anodic polarization in Alkaline Solutions Containing H2S

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

INFLUENCE OF SATURATED H_2S ON CORROSION BEHAVIOR OF 316L STAINLESS STEEL

Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions

Electrochemical Study of External Corrosion of Three API Steels Exposed to Seawater and Sediment from Seabed of the Gulf of México

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion Mechanism of Oil Field Gathering Pipeline Containing Small H2S Impurity

The corrosion behaviour of sulphur on the carbon steel used in oil & gas field with high concentration of H2S

Effect of interaction between corrosion film and H2S/CO2 partial pressure ratio on the hydrogen permeation in X80 pipeline steel

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

The Influence of Hydrogen Sulfide on Corrosion of Iron under Different Conditions

Dissolution kinetics of the sulfide-oxide complex inclusion and resulting localized corrosion mechanism of X70 steel in deaerated acidic environment

Effect of Ti Microalloying on the Corrosion Behavior of Low-Carbon Steel in H2S/CO2 Environment

Impact of multi-factor coupling on the corrosion behavior of 254SMo stainless steel in an aggressive oilfield environment containing CO 2 and H 2 S

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Impact of Multi-Factor Coupling on the Corrosion Behavior of 254smo Stainless Steel in an Aggressive Oilfield Environment Containing Co2 and H2s

Investigation of the Effect of pH on Stress Corrosion Cracking of API 5L X65 Steel by Impedance Spectroscopy and Slow Strain Rate Tensile Test