Abstract:Large enhancements of the melt strength of polypropylene (PP) were achieved by the introduction of specific unsaturated linear polyester (ULP) branches using melt grafting. The transient torque curves and optical rheology microscope images indicated that branching reactions took place and the ULP had been grafted onto the PP backbone. Shear rheological behaviors of three kinds of PP were investigated using rotational rheometer under dynamic shear mode with periodic shear rate. These PP samples are foamable PP (FPP) with sparse branches obtained by grafting ULP, commercial high melt strength PP (HMS PP) for foaming and conventional linear PP (EPS). It was found that the rheological properties of FPP, the HMS PP, were distinctly different from those of conventional PP. Storage modulus, steady state compliance and zero shear viscosity increased in comparison with EPS, while shear viscosity decreased. This result implied the presence of branching structures that was not revealed in conventional PP. In melt flow measurements, extrusion swell that was a prominent behavior of branching PP was observed also for FPP and PF. Compared to linear PP, FPP and PF showed distinct sag-resistant property and lower melt flow index. On the other hand, to estimate the extent of branching, a detailed method was applied using the obtained zero shear viscosity. The result showed that FPP was grafted by sparse ULP. From these results, it was found that FPP showed obvious enhancements in rheological behaviors similar to PF, although its melt strength was lower than that of PF due to the presence of shorter branching chains grafted on the backbone of FPP.

Preparation and foamability of high melt strength polypropylene based on grafting vinyl polydimethylsiloxane and styrene

A Novel Strategy for Achieving High Melt Strength Polypropylene and an Investigation of Its Foamability

Rheology and Foaming Properties of High Melt Strength Polypropylene Based on Styrene/Acrylic Silicone Oil

Study on Melt-Grafting of Maleic Anhydride Onto Polypropylene in the Presence of Styrene

Polydimethylsiloxane Assisted Supercritical CO 2 Foaming Behavior of High Melt Strength Polypropylene Grafted with Styrene

Rheological, crystallization and foaming behaviors of high melt strength polypropylene in the presence of polyvinyl acetate

Enhancing the Sound and Thermal Insulation Properties of Polypropylene Foam by Preparing High Melt Strength Polypropylene

Effects of In Situ Addition α Nucleating Agent on Properties of High Melt Strength Polypropylene

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Design of Well-Defined Polyethylene-g-poly-methyltrifluorosiloxane Graft Copolymers Via Direct Copolymerization of Ethylene with Polyfluorosiloxane Macromonomers

Preparation and properties of polypropylene modified by grafting styrene

High melt strength polypropylene by ionic modification: Preparation, rheological properties and foaming behaviors

Synergistic effect of styrene and zinc dimethyldithiocarbamate on the properties of high melt strength polypropylene

Crystallization Behaviors and Mechanical Properties of Polypropylene Grafted by Vinyl Silane/Styrene

The Characterization of Rheological Properties of Melt Grafting Polypropylene for Foaming

Influence Of Grafting Formulations And Extrusion Conditions On Properties Of Silane-Grafted Polypropylenes

Preparation of Long Chain Branched Pp Via Multi-Monomer Melt Grafting in the Presence of Bi-Functional Monomer 1,6-Hexanediol Diacrylate

Study of Melt Free Radical Grafting of Maleic Anhydride and Styrene Onto Polypropylene and Its Properties

Melt Grafting of Vinyltrimethoxysilane and Water Crosslinking of Polypropylene/Ethylene-Propylene Diene Terpolymer Blends

Grafting of Polypropylene with N-Cyclohexylmaleimide and Styrene Simultaneously Using Supercritical Co2

Preparation of high-expanded PP foams with chemical blowing process