Preparation of hierarchical porous carbons from amphiphilic poly(vinylidene chloride- co -methyl acrylate)- b -poly(acrylic acid) copolymers by self-templating and one-step carbonization method

jie yang,yongzhong bao,pengju pan

DOI: https://doi.org/10.1016/j.micromeso.2014.05.012

IF: 5.876

2014-01-01

Microporous and Mesoporous Materials

Abstract:Based on our previous proposed method to fabricate the hierarchical porous carbons (HPCs), a series of amphiphilic poly(vinylidene chloride-co-methyl acryalte)-b-poly(acrylic acid) (PVDC-b-PAA) copolymers were prepared via RAFT polymerization and used to prepare the HPCs by self-templating and one-step carbonization method. The phase structure and thermal degradation behavior of PVDC-b-PAA copolymers, as well as the morphology and pore structure of corresponding carbons were investigated. It was found that all block copolymers exhibited micro-phase separation feature and showed the PAA-dispersed, bi-continuous, and PAA-dominated phase structures as the PVDC/PAA molar ratio varied from 3:1 to 0.77:1. Although the PVDC-b-PAA copolymers exhibited the individual glass transitions of each block, the thermal degradations of PVDC and PAA blocks were interacted and overlapped. The carbons prepared from PVDC-b-PAA contained the micro- and meso-pores, which were mainly originated from the thermal degradation of PVDC segment and the pyrolysis of FAA segment, respectively. The carbons prepared from PVDC66-b-PAA(22) copolymer exhibited a maximum Brunauer-Emmett-Teller surface area of 1093 m(2) and a maximum total pore volume of 0.51 cm(3) g(-1). Due to the incomplete pyrolysis of FAA segment and the jamming effect to pores caused by the PAA-based carbon, the total pore volume of HPCs prepared from PVDC-b-PAA copolymers were lower than that of HPCs prepared from the PVDC-b-polystyrene copolymers. (C) 2014 Elsevier Inc. All rights reserved.