Preparation and characterization of vinylidene chloride copolymer/nanometer hydrotalcite composites and porous carbons

Qiqiang WU,Yongzhong BAO

2011-01-01

Abstract:To prepare porous carbons with meso-pores, nanometer hydrotalcite (HT) particles were incorporated into vinylidene chloride-methyl acrylate (VDC-MA) copolymer by in-situ suspension polymerization and further melt processing. Porous carbons with meso-pores were obtained by high-temperature carbonization of the VDC-MA copolymer/HT composites and removing of inorganic particles. The composites and the resultant porous carbons with meso-pores were characterized by electron microscope, X-ray diffraction, and nitrogen adsorption/desorption analysis. The results showed that most HT particles were dispersed in the VDC-MA copolymer matrix in nanometer size, when the mass fraction of HT was ≤6.25%. HT was transformed to metal oxides during the carbonization process, which was easy to remove by acid etching and acted as template to form meso-pores. During the carbonization process, micro-pores were also formed due to the thermal degradation of VDC copolymer. When carbonization temperature was lower (600-700°C), VDC-MA copolymer could not be degraded completely, and the specific surface area and porosity of the resulted carbon were lower. When carbonization temperature was 800°C, the carbons prepared from composites with different HT contents had specific surface areas of about 1000 m 2·g -1. The maximum degree of meso-porosity was 26.5% for the carbon prepared from VDC-MA copolymer/HT composite with 6.25%(mass) HT.