Hierarchical Porous Structure Formation Mechanism in Food Waste Component Derived N-doped Biochar: Application in VOCs Removal.

Yuxuan Yang,Chen Sun,Qunxing Huang,Jianhua Yan

DOI: https://doi.org/10.1016/j.chemosphere.2021.132702

IF: 8.8

2022-01-01

Chemosphere

Abstract:Nitrogen-doped (N-doped) hierarchical porous carbon was widely utilized as an efficient volatile organic compounds (VOCs) adsorbent. In this work, a series of N-doped hierarchical porous carbons were successfully prepared from the direct pyrolysis process of three food waste components. The porous biochar that derived from bone showed a high specific surface area (1405.06 m(2)/g) and sizable total pore volume (0.97 cm(3)/g). The developed hierarchical porous structure was fabricated by the combined effect of self-activation (Carbon dioxide (CO2) and water vapor (H2O)) and self-template. The emission characteristics of activation gas analyzed by Thermogravimetric-Fourier transform infrared spectrometer (TG-FTIR) and the transformation of ash composition in the biochar help to illustrate the pore-forming mechanism. Calcium oxide (CaO) and hydroxylapatite were confirmed as the major templates for mesopores, while the decomposition processes of calcium carbonate (CaCO3) and hydroxylapatite provided a large amount of activation gas (CO2 and H2O) to form micropores. The materials also obtained abundant N-containing surface functional groups (up to 7.84 atomic%) from pyrolysis of protein and chitin. Finally, the porous biochar showed excellent performance for VOCs adsorption with a promising uptake of 288 mg/g for toluene and a high adsorption rate of 0.189 min(-1). Aplenty of mesopores distributed in the materials effectively improved the mass transfer behaviors, the adsorption rate got a noticeable improvement (from 0.118 min(-1) to 0.189 min(-1)) benefited from mesopores. Reusable potentials of the hierarchical porous carbons were also satisfying. After four thermal regeneration cycles, the materials still occupied 84.8%-87.4% of the original adsorption capacities.