Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Effects of Grain Size on the High-Cycle Fatigue Behavior of In792 Superalloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effects of Grain Refinement on the Low-Cycle Fatigue Behavior of IN792 Superalloys

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

A study of high cycle fatigue life and its correlation with microstructural parameters in IN713C nickel-based superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Grain Size Effect on the Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169

Effects of Grain Sizes on Small Fatigue Crack Growth of GH4169 Ni-base Alloy

Effect of Inclusion Size and Distribution on Low Cycle Fatigue Properties of an FGH97 Superalloy

Low Cycle Fatigue and High Cycle Fatigue of K4750 Ni-based Superalloy at 600 °C: Analysis of Fracture Behavior and Deformation Mechanism

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Influence of Grain Size on the Small Fatigue Crack Initiation and Propagation Behaviors of a Nickel-Based Superalloy at 650 °C

Microstructures' Effects on High Temperature Fatigue Failure Behavior of Typical Superalloys

Low cycle fatigue behaviors of CrCoNi medium-entropy alloy with different grain sizes

Effect of micro-grain casting process on the microstructure and high cycle fatigue properties of K492M alloy at 700 °C

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Effect of Grain Size on High Temperature Oxidation Behavior of IN792 Superalloy

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

High-Temperature Low-Cycle Fatigue Properties of GH4169 Ni-based Superalloy