An investigation of residual stresses in brazed cubic boron nitride abrasive grains by finite element modelling and raman spectroscopy

yejun zhu,wenfeng ding,jiuhua xu,changyong yang

DOI: https://doi.org/10.1016/j.matdes.2015.08.039

IF: 9.417

2015-01-01

Materials & Design

Abstract:Joining cubic boron nitride (CBN) abrasive grains and tool body made of steel using brazing always creates residual stress due to thermal mismatch of the components when cooling down from the brazing temperature. A large tensile stress perhaps causes grain fracture during the grinding process with single-layer brazed CBN abrasive tools. To evaluate the residual stresses occurring in brazed CBN grains, values and distribution of residual stresses are calculated using the finite element method. Effects of bonding materials, embedding depth, gap thickness and grain size on brazing-induced residual stresses are discussed. Results show that the Cu–Sn–Ti bonding alloy always results in a larger tensile stress in the CBN grains, when compared to Ag–Cu–Ti alloy during the cooling phase of the brazing process. The maximum tensile stress is obtained at the grain–bond junction region irrespective of the choice of bonding material and embedding depth. When the grain side length is 100μm, gap thickness is 10μm and grain embedding depth is 30%, the maximum magnitude of the tensile stresses is obtained. The maximum stress is 401MPa with Ag–Cu–Ti alloy and 421MPa with Cu–Sn–Ti alloy. The brazing-induced residual stresses have been finally measured experimentally by means of the Raman spectroscopy. The current simulated results are accordingly verified valid.