Preparation of Calcium Sulfate Whiskers from FGD Gypsum Via Hydrothermal Crystallization in the H2SO4–NaCl–H2O System

Xiao Wang,Liushuan Yang,Xinfeng Zhu,Jiakuan Yang

DOI: https://doi.org/10.1016/j.partic.2013.12.001

2014-01-01

Abstract:Little attention has thus far been paid to the potential effect of solution composition on the hydrothermal crystallization of calcium sulfate whiskers prepared from flue-gas desulfurization（FGD） gypsum.When purified FGD gypsum was used as raw material,the morphology and phase structure of the hydrothermal products grown in pure water,H 2 SO 4 -H 2 O,NaCl-H 2 O,and H 2 SO 4 -NaCl-H 2 O solutions as well as the solubility of purified FGD gypsum in these solutions were investigated.The results indicate that calcium sulfate whiskers grow favorably in the H 2 SO 4 -NaCl-H 2 O system.When prepared using 10-70 g NaCl/kg gypsum-0.01 M H 2 SO 4 -H 2 O at 130 ℃ for 60 min,the obtained calcium sulfate whiskers had diameters ranging from 3 to 5 |xm and lengths from 200 to 600 |xm,and their phase structure was calcium sulfate hemihydrate（HH）.Opposing effects of sulfuric acid and sodium chloride on the solubility of the purified FGD gypsum were observed.With the co-presence of sulfuric acid and sodium chloride in the reaction solution,the concentrations of Ca 2+ and SO 4 2- can be kept relatively stable,which implies that the crystallization of the hydrothermal products can be controlled by changing the concentrations of sulfuric acid and sodium chloride.