EFFECT OF PHASE SEPARATION ON DYNAMIC VISCOELASTICITY OF POLY (METHYL METHACRYLATE)/POLY (Α-Methylstyrene-co-acrylonitrile) BLENDS

O Araki,Q Zheng,M Takahashi,T Takigawa,T Masuda

DOI: https://doi.org/10.2472/jsms.44.504appendix_144

1995-01-01

Abstract:Blends of Poly(methyl methacrylate) (PMMA) and poly(alpha-methylstyrene-co-acrylonitrile) (alpha MSAN) exhibit an LCST behavior and are miscible at lower temperatures than the cloud points. The temperature dispersion of dynamic viscoelasticity of the blend system was measured in the single-phase and phase-separated states. It was found that some thermal histories during sample preparation bring the structural equilibrium to PMMA and alpha MSAN. Such a thermal condition was used for all the measurements to attain the experimental reproducibility. Temperature dispersion curves of dynamic viscoelastic functions, E', E '' and tan delta, for the blends in single-phase and phase-separated cases located between those of PMMA and alpha MSAN in order of the component ratio. The shapes of the curves of phase-separated blends, however, become quite different from those of single-phase ones at temperatures above 80 degrees C. The curves of E' and tan delta of blend samples in phase-separation show the broad relaxation and locate close to those of the rich component. Correspondingly, the peaks of the E '' curves of phase-separated samples become broader than those for single-phase. Only the PMMA/alpha MSAN(40/60) blend in a phase-separated state shows two peaks on the E '' curve when it was annealed at 200 degrees C. These two peaks become more apparent with the annealing time suggesting the phase separation proceeds.