Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Effect of CaO on the selective non-catalytic reduction deNO x process: Experimental and kinetic study

The development of Fe2O3-based catalysts used for the selective catalytic reduction of NOx with NH3: A review

Mechanism Study on the Adsorption and Reactions of NH3, NO, and O2 on the CaO Surface in the SNCR Denox Process

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Study On The Influence Of Cao On Nh3+No+O-2 Reaction System In Pre-Calciner

DFT Study of the Effect of Ca on NO Heterogeneous Reduction by Char

Influence of CaCO_3 on NH_3 Oxidation

@Experimental Study of the Influence of CaCO3on NH3+NO+O2 Reaction System

Study on the Catalysis of CaCO3 in the SNCR Denox Process for Cement Kilns

Mechanism of the Reaction Between HNCO and CaO in the Urea-Selective Non-catalytic Reduction Denox Process

Effect Of Sulfated Cao On No Reduction By Nh3 In The Presence Of Excess Oxygen

Effect of Sulfated CaO on NO Reduction by NH<sub>3</sub>in the Presence of Excess Oxygen

Experimental and Kinetic Study on the Influence of Iron Oxide on the Selective Noncatalytic Reduction Deno(X) Process

DRIFTS study of ammonia activation over CaO and sulfated CaO for NO reduction by NH3.

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Experimental and Kinetic Study on the Influence of CaO on the N2O + NH3 + O2 System

Calcium poisoning mechanism on the selective catalytic reduction of NOx by ammonia over the γ-Fe2O3 (001) surface

Effect of Cao on Nh3+ No + O-2 Reaction System in the Absence and Presence of High Concentration Co2

NH_3 Oxidation Using SNCR to Control Cement Kiln NO_x

Influence of Calcium-Based Particles on the Selective Non-Catalytic Reduction Process in a Pre-Calciner

Influence of CaO on Urea Pyrolysis in the Selective Non-Catalytic Reduction Denox Process