Abstract:The aim of the study was to develop a design methodology for the UltraHigh Molecular Weight Polyethylene (UHMWPE)-based composites used in friction units. To achieve this, stress–strain analysis was done using computer simulation of the triboloading processes. In addition, the effects of carbon fiber size used as reinforcing fillers on formation of the subsurface layer structures at the tribological contacts as well as composite wear resistance were evaluated. A structural analysis of the friction surfaces and the subsurface layers of UHMWPE as well as the UHMWPE-based composites loaded with the carbon fibers of various (nano-, micro-, millimeter) sizes in a wide range of tribological loading conditions was performed. It was shown that, under the “moderate” tribological loading conditions (60 N, 0.3 m/s), the carbon nanofibers (with a loading degree up to 0.5 wt.%) were the most efficient filler. The latter acted as a solid lubricant. As a result, wear resistance increased by 2.7 times. Under the “heavy” test conditions (140 N, 0.5 m/s), the chopped carbon fibers with a length of 2 mm and the optimal loading degree of 10 wt.% were more efficient. The mechanism is underlined by perceiving the action of compressive and shear loads from the counterpart and protecting the tribological contact surface from intense wear. In doing so, wear resistance had doubled, and other mechanical properties had also improved. It was found that simultaneous loading of UHMWPE with Carbon Nano Fibers (CNF) as a solid lubricant and Long Carbon Fibers (LCF) as reinforcing carbon fibers, provided the prescribed mechanical and tribological properties in the entire investigated range of the “load–sliding speed” conditions of tribological loading.

Wear and Friction of Carbon Nanofiber-Reinforced Hdpe Composites

Tribological Behavior of High Density Polyethylene Nanocomposites with Silane Treated Carbon Nanofibers

Wear of Carbon Nanofiber Reinforced HDPE Nanocomposites Under Dry Sliding Condition

Comparison Of Tribological Performances Of High Density Polyethylene Enhanced With Carbon Nanofibers

Mechanical Properties, Tribological Behavior, and Biocompatibility of High-Density Polyethylene/carbon Nanofibers Nanocomposites

Friction and Wear Characteristics of Additive Manufactured CNT-Reinforced HDPE Composites in Dry Contact

High-Temperature Tribological Behavior of HDPE Composites Reinforced by Short Carbon Fiber under Water-Lubricated Conditions

Structure, Mechanical Properties and Friction Behavior of UHMWPE/HDPE/carbon Nanofibers

Effect of reinforcement on wear debris of carbon nanofiber/high density polyethylene composites: Morphological study and quantitative analysis

Nanoscale Characterization of Wear Particles Produced from CNF-Reinforced HDPE Composites

Sensitivity of Dielectric Properties to Wear Process on Carbon Nanofiber/High-Density Polyethylene Composites.

Tribological Behavior of Carbon-Nanotube-Filled PTFE Composites

Tribological properties of carbon nanotube-doped carbon/carbon composites

Study on the Tribological Properties of Carbon Fabric/Polyimide Composites Filled with SiC Nanoparticles

Tribological Properties of Carbon Nanotube-Reinforced Composites

Enhanced Wear Resistance of High-Density Polyethylene Composites Reinforced by Organosilane-Graphitic Nanoplatelets

Study of the Electrical and Tribologic Properties of CNTs-HDPE Composites

The Reduction in the Deformation of HDPE Composites Using Self-Lubricating Fillers in an Aqueous Environment

Increasing Wear Resistance of UHMWPE by Loading Enforcing Carbon Fibers: Effect of Irreversible and Elastic Deformation, Friction Heating, and Filler Size

Surface Mechanical Characterization of Carbon Nanofiber Reinforced Low-Density Polyethylene by Nanoindentation and Comparison with Bulk Properties

Friction and wear behavior of polyimide matrix composites filled with nanographite