Self-organised nanoporous anodic films on superaustenitic stainless steel

wenlian lu,dixin zou,y han,rui liu,c tian

DOI: https://doi.org/10.1179/1432891714Z.000000000776

2014-01-01

Materials Research Innovations

Abstract:Self-organised nanoporous anodic films were fabricated on 904L superaustenitic stainless steel by the electrochemical treatment in ethylene glycol electrolyte containing perchloric acid. The effects of experimental conditions, such as electrolyte temperature and applied voltage on nanoporous morphology, were studied by the way of scanning electron microscopy. The results show that lower solution temperature promotes formation of orderly nanopores. Nanoporous anodic films cannot be formed, and pitting will appear on the stainless steel when temperature is above 40 degrees C. The sizes of pores gradually increase with increasing applied voltage when the applied voltage is lower than 30 V. Porous morphology will change from roughly circular to polygonal, and the size will change from uniform to uneven when the applied voltage is higher than 30 V. It is difficult to form orderly nanoporous anodic films when the applied voltage is too high. Difference of element content in stainless steel is also an important factor for the porous morphology. When the applied voltage is 50 V, orderly pores are formed on 316 austenitic stainless steel surface. However, under the same conditions, this phenomenon does not occur on 904L superaustenitic stainless steel surface. From the analysis of X-ray photoelectron spectroscopy, the films are composed of various metal oxides.