Abstract:Currently, it is still a great challenge to obtain copper-based high-efficient dropwise condensation heat transfer (CHT) interfaces via template-free electrodepositing technologies. Here, we report that the density of template-free electrodeposited copper nanocones can maximally reach 1.5 × 106/mm2 by the synergistic control of substrate surface roughness, poly(ethylene glycol) (PEG) molecular weight, and PEG concentration. After thiol modification, the densely packed copper nanocone samples can present low-adhesive superhydrophobicity and condensate microdrop self-jumping function at ambient environment. Condensation heat and mass transfer characterizations show that the CHT coefficient of copper surfaces can maximally enhance 98% for 20 °C vapor and 51% for 40 °C vapor by in situ growth of superhydrophobic densely packed copper nanocones. Although the dropwise condensation mode can change from the jumping mode to the mixed jumping and sweeping mode and the shedding-off mode along with the increase of surface subcooling and vapor temperature, the CHT performance of the nanosample is still superior to that of the contrast flat hydrophobic surface during the whole testing range of surface subcooling. As vapor temperature increases to 80 °C, the CHT performance of the nanosample is inferior to that of the contrast sample. The CHT enhancement under low-temperature vapor should be ascribed to the enhancement of small-drop mass transfer ability caused by low-adhesive superhydrophobicity nature of nanosample surfaces. Their performance degradation mainly results from increased drop-drop drag force along with the increase of surface subcooling and vapor temperature. In sharp contrast, the CHT deterioration under high-temperature vapor should be ascribed to larger drop-surface adhesion and drop-drop drag force. The former is caused by vapor penetration, whereas the latter is caused by the dramatically increased nucleation density and growth rate of condensates. These findings would help design and develop copper-based high-efficiency condensation heat transfer interfaces.

Electrodeposition and Characterization of Copper Nanocone Structures

Cuprite Nanowires by Electrodeposition from Lyotropic Reverse Hexagonal Liquid Crystalline Phase

Formation of nanostructured copper filaments in electrochemical deposition.

Electrochemical Approach Towards the Controllable Synthesis of Nickel Nanocones Based on the Screw Dislocation

Density Maximization of One-Step Electrodeposited Copper Nanocones and Dropwise Condensation Heat-Transfer Performance Evaluation

Achieving of Bionic Super-Hydrophobicity by Electrodepositing Nano-Ni-pyramids on the Picosecond Laser-Ablated Micro-Cu-cone Surface

Structure and Properties of Electrocodeposited Cu-Al2o3 Nanocomposite Thin Films

In Situ Study of Copper Electrodeposition on A Single Carbon Fiber

Superhydrophobic Ni nanocone surface prepared by electrodeposition and its overall performance

Electrodeposition: Small 20/2009

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

Facile Electrochemical Synthesis of Single-Crystalline Copper Nanospheres, Pyramids, and Truncated Pyramidal Nanoparticles from Lithia/Cuprous Oxide Composite Thin Films

An Additive-Free Electrochemical Route to Rapid Synthesis of Large-Area Copper Nano-Octahedra on Gold Film Substrates

Electrodeposition of Novel Nanostructured Materials Using Mesoporous Silica Thin Films As Templates

Extreme wettability due to dendritic copper nanostructure via electrodeposition

Electrochemical Synthesis of Copper Sulfide Nanostructure with PAM Hydrogel Template

Uniform Electrochemical Deposition of Copper onto Self-Assembled Gold Nanoparticles

In Situ Visual Observation of Surface Energy-Controlled Heterogeneous Nucleation of Metal Nanocrystals

Dialectical Observation of Controllable Electrodeposited Ni Nanocones: the Unification of Local Disorder and Overall Order

Copper Hydroxide Nanoneedle And Nanotube Arrays Fabricated By Anodization Of Copper

Ultra-high flatness and conductivity of copper electrodeposits obtained by nano-twinned/fine-grained double layer electrodeposition