Abstract:In this study, three cationic surfactants (hexadecyltrimethylammonium chloride, hexadecyldimethylbenzylammonium chloride, and octadecyltrimethylammonium chloride) were used to modify montmorillonite and polyethylene (PE)/maleic anhydride grafted polyethylene (PE-g-MAH)/organic-montmorillonite (Org-MMT) nano-composites, prepared by two blending processes (direct-melt blending and solution blending). X-ray diffractometry and transmission electron microscopy were used to investigate the intercalation behavior and microstructure of composites. Mechanical properties were also tested. It was found that the intercalation effect of PE/PE-g-MAH/Org-MMT could be enhanced by increasing the content of PE-g-MMT, using the silicate modified by a cationic surfactant with a benzyl group or long alkyl chain, adopting the solution-blending method or using high-density polyethylene as matrix. The degree of crystallinity of composites and the crystalline thickness perpendicular to the crystalline plane [like (110) and (200)] decreased with increasing amounts of PE-g-MAH and, under certain prescription, the crystalline thickness of the composite made by the solution method was much smaller than that made by direct-melt blending. This clearly showed that Org-MMT and PE-g-MAH had a heterogeneous nucleation effect on crystallization of PE from the melt, resulting in a decrease of crystalline thickness, and the heterogeneous nucleation effect was more evident in the nanocomposite made by the solution-blending method than in that made by the direct-melt intercalation process. The tensile strength initially increased and then decreased with increasing contents of PE-g-MAH. The maximum value in tensile strength (23.3 MPa) was achieved when the concentration of PE-g-MAH was 6 wt %. The impact strength increased concomitantly with the content of PE-g-MAH; it was 122.2 J/m when the concentration of PE-g-MAH was 9 wt %. (C) 2004 Wiley Periodicals, Inc.

Improved Mechanical Properties of Montmorillonite/Nylon 6 Nanocomposites by the Modification of Novolac

In-situ Synthesis, Thermal and Mechanical Properties of Biobased Poly(ethylene 2,5-Furandicarboxylate)/montmorillonite (PEF/MMT) Nanocomposites

Preparation and Properties of PA6/Epoxy-resin-modified Montmorillonite Nanocomposites

Combination of double-modified clay and polypropylene-graft-maleic anhydride for the simultaneously improved thermal and mechanical properties of polypropylene

Preparation and characterization of organic modified montmorillonite/polylactic acid nanocomposites

Triglycidyl Para -Aminophenol Modified Montmorillonites for Epoxy Nanocomposites and Multi-Scale Carbon Fiber Reinforced Composites with Superior Mechanical Properties

Thermal–oxidative Degradation and Accelerated Aging Behavior of Polyamide 6/epoxy Resin‐modified Montmorillonite Nanocomposites

The Structure and Properties of PA6/MMT Nanocomposites Prepared by Melt Compounding

Preparation of Poly(Phenylene Oxide)/Polyamide-6 Nanocomposites with High Tensile Strength and Excellent Impact Performance

Study on thermal stability of PP/MMT nanocomposites

Percolation Network Formation in Nylon 6/Montmorillonite Nanocomposites: A Critical Structural Insight and the Impact on Solidification Process and Mechanical Behavior

Polyethylene/maleic Anhydride Grafted Polyethylene/organic‐montmorillonite Nanocomposites. I. Preparation, Microstructure, and Mechanical Properties

Preparation and Characterization of Nylon 66/montmorillonite Nanocomposites with Co-Treated Montmorillonites

Joint Effect of Compatibilizer and Organo-Montmorillonite on Compatibilization of Polyamide-6/Poly(Phenylene Oxide) Blend: Morphology and Properties

Polyamide-6/montmorillonite Nanocomposites Toughened with ABS-g-MA Core-Shell Structural Particles

Preparation and Characterization of Polyamide 66/montmorillonite Nanocomposites with Methyl Methacrylate As Cointercalation Agent

Effect of Organo-Montmorillonite on the Compatibility of Polyamide 66/polypropylene Blend

Effect of Dendrimer‐like PAMAM Grafted Attapulgite on the Microstructure and Morphology of Nylon‐6

Water-Assisted Melt Compounding Preparation and Property of Nylon6/Nano-MMT Masterbatch

Melt rheological properties of nylon 6/multi-walled carbon nanotube composites

Preparation and properties of nylon 11/ethylene‐vinyl alcohol/montmorillonite ternary composites