Abstract:Hollow titanium dioxide (TiO 2 ) microspheres were synthesized in one step by employing tetrabutyl orthotitanate (TBOT) as a precursor through a facile solvothermal method in the presence of NH 4 HCO 3 . XRD analysis indicated that anatase TiO 2 can be obtained directly without further annealing. TiO 2 hollow microspheres with diameters in the range of 1.0–4.0 μm were confirmed through SEM and TEM measurements. The specific surface area was measured to be 180 m 2 g −1 according to the nitrogen adsorption–desorption isotherms. Superior photocatalytic performance and good lithium storage properties were achieved for resultant TiO 2 samples. The H 2 evolution rate of the optimal sample is about 0.66 mmol h −1 after loaded with 1 wt.% Pt (20 mg samples). The reversible capacity remained 143 mAh g −1 at a specific current of 300 mA g −1 after 100 charge–discharge cycles. This work provides a facile strategy for the preparation of hollow titanium dioxide microspheres and demonstrates their promising photocatalytic H 2 evolution and the lithium storage properties. Graphical abstract Hollow titanium dioxide spheres are directly synthesized via a facile template-free solvothermal method with the presence of NH 4 HCO 3 based on inside-out Ostwald ripening (see picture), and demonstrated both as a photocatalyst for water splitting and a promising anode material for lithium-ion batteries. Superior photocatalytic performance and excellent lithium storage properties are achieved for resultant TiO 2 hollow microspheres.

Facile Synthesis of Porous Microspheres Composed of TiO2 Nanorods with High Photocatalytic Activity for Hydrogen Production

Hierarchical Spheres Assembled from Large Ultrathin Anatase TiO2 Nanosheets for Photocatalytic Hydrogen Evolution from Water Splitting

Cocatalyzing Pt/PtO Phase-Junction Nanodots on Hierarchically Porous TiO2 for Highly Enhanced Photocatalytic Hydrogen Production.

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Synthesis and Photocatalytic Activity of Porous Anatase TiO2 Microspheres Composed of {010}-Faceted Nanobelts

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Octahedral Shaped PbTiO 3 -TiO 2 Nanocomposites for High-Efficiency Photocatalytic Hydrogen Production.

Direct fabrication of anatase TiO 2 hollow microspheres for applications in photocatalytic hydrogen evolution and lithium storage

Yolk-Shell Tio2-Nrs@Sio2 with Enhanced Photocatalytic Hydrogen Production

Gelatin-assisted Sol–gel Derived TiO2 Microspheres for Hydrogen Storage

Hydrothermal growth of multi-facet anatase spheres

Hierarchical Nanosheet-Assembled Yolk–shell TiO2microspheres with Improved Photocatalytic Activity

Hydrogenated TiO2/SrTiO3 porous microspheres with tunable band structure for solar-light photocatalytic H2 and O2 evolution

Synthesis of Uniform Ordered Mesoporous TiO2 Microspheres with Controllable Phase Junctions for Efficient Solar Water Splitting

Porous TiO2 Hollow Nanospheres: Synthesis, Characterization and Enhanced Photocatalytic Properties

A Facile and Waste-Free Strategy to Fabricate Pt-C/TiO2 Microspheres: Enhanced Photocatalytic Performance for Hydrogen Evolution

Formation of Monodispersed Anatase Tio2 Spheres from Tioso4 for Enhanced Hydrogen Evolution of Tio2/G-C3n4 Photocatalysts

Fabrication of porous titanium dioxide fibers and their photocatalytic activity for hydrogen evolution

Formation of hollow porous TiO2 nanospheres via the encapsulation of CO2 nanobubbles for high-performance adsorption and photocatalysis

Carbon-incorporated TiO2 microspheres: Facile flame assisted hydrolysis of tetrabutyl orthotitanate and photocatalytic hydrogen production