Abstract:A series of manganese-based catalysts supported by 5-10 nm, 10-25 nm, 40 nm and 60 nm anatase TiO2 particles was synthesized via an impregnation method to investigate the effect of the initial support particle size on the selective catalytic reduction (SCR) of NO with NH3. All catalysts were characterized by transmission electron microscopy (TEM), N2 physisorption/desorption, X-ray diffraction (XRD), temperature programmed techniques, X-ray photoelectron spectroscopy (XPS) and in situ diffuse reflectance infrared transform spectroscopy (DRIFTS). TEM results indicated that the particle sizes of the MnO x /TiO2 catalysts were similar after the calcination process, although the initial TiO2 support particle sizes were different. However, the initial TiO2 support particle sizes were found to have a significant influence on the SCR catalytic performance. XPS and NH3-TPD results of the MnO x /TiO2 catalysts illustrated that the surface Mn4+/Mn molar ratio and acid amount could be influenced by the initial TiO2 support particle sizes. The order of surface Mn4+/Mn molar ratio and acid amount over the MnO x /TiO2 catalysts was as follows: MnO x /TiO2(10-25) > MnO x /TiO2(40) > MnO x /TiO2(60) > MnO x /TiO2(5-10), which agreed well with the order of SCR performance. In situ DRIFTS results revealed that the NH3-SCR reactions over MnO x /TiO2 at low temperature occurred via a Langmuir-Hinshelwood mechanism. More importantly, it was found that the bridge and bidentate nitrates were the main active substances for the low-temperature SCR reaction, and bridge nitrate adsorbed on Mn4+ showed superior SCR activity among all the adsorbed NO x species. The variation of the initial TiO2 support particle size over MnO x /TiO2 could change the surface Mn4+/Mn molar ratio, which could influence the adsorption of NO x species, thus bringing about the diversity of the SCR catalytic performance.

Mn Promoted Pd/Tio2-Al2o3 Catalyst For The Selective Catalytic Reduction Of Nox By H-2

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

In Situ Hydrogen Uptake and NOx Adsorption on Bifunctional Heterogeneous Pd/Mn/Ni for a Low Energy Path Toward Selective Catalytic Reduction

H3pw12o40-Modified Mnox: Efficient Catalyst for Nh3-Scr of Nox

Eu-Mn-Ti Mixed Oxides for the SCR of NOx with NH3: the Effects of Eu-modification on Catalytic Performance and Mechanism

Promoting Effect of Polyoxometallic Acid Modification on the NH3-SCR Performance of Mn-Based Catalysts

Selective catalytic reduction of NOx by H2 over Pd/TiO2 catalyst

Selective catalytic reduction of NOx by H2 over Na modified Pd/TiO2 catalyst

Selective catalytic reduction of NOx with NH3 over Mn–Zr–Ti mixed oxide catalysts

Study on the Role of Mn Species in Low Temperature SCR on MnOx/TiO2 Through Experiment and DFT Calculation

Promoting effect of polyoxometallic acid modification on the NH 3 -SCR performance of Mn-based catalysts

Phosphotungstic Acid-Modified MnOx for Selective Catalytic Reduction of NOx with NH3

Selective catalytic reduction of NOx by H2 over a novel Pd/FeTi catalyst

Effect of Mn Loading on Catalytic Performance of Nmno/tio in NH-SCR Reaction

Phosphotungstic Acid-Modified MnO<sub>x</sub> for Selective Catalytic Reduction of NO<sub>x</sub> with NH<sub>3</sub>

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Effect of Initial Support Particle Size of MnOx/TiO2 Catalysts in the Selective Catalytic Reduction of NO with NH3

Understanding The Promotional Effect Of 3d Transition Metals (Fe, Co, Cu) On Pd/Tio2 For H-2-Scr

Study on H2O2, Ce, W modified MnO /TiO2 based NH3-SCR Catalyst: The status and effect of doped promoters and synergies

Selective catalytic reduction of nitrogen oxides by methane over Ni/H-USY catalysts

Mechanism and regeneration of sulfur-poisoned Mn-promoted calcined NiAl hydrotalcite-like compounds for C3H6-SCR of NO