Abstract:Two types spherical-like SiO2 with different specific surface area (SSA) and porosity were synthesized and used as support for Pd catalysts, which were prepared by various protocols (in situ synthesis (IS, Pd/S-1(IS), and Pd/S2(IS)), we impregnation (WI, Pd/S-1(WI) , and Pd/S-2(WI)), and grafting (GA, Pd/S-1(GA), and Pd/S-2(GA))) and adopted in n-butylamine combustion. Results suggest that Pd dispersion is positive correlation with support SSA and GA method is the most favorable approach to obtain highly dispersed Pd active sites. Pd/S-1(IS), Pd/S-1(WI) and Pd/S1(GA )catalysts with small SSA show inferior activity and higher NOx yield than those of Pd/S-2(IS), Pd/S-2(WI), and Pd/S-2(GA) with large SSA, irrelevant with the preparation methods. Amongst, Pd/S-2(GA) possesses the smallest Pd average diameter (ca. 1.72 nm) and highest activity with 90% of n-butylamine destructed at 234 degrees C; however, the yield of NOx over Pd/S-2(GA) is much higher than the other catalysts (except Pd/S-1(GA)) as the GA approach provides high concentration of active sites and the preparation procedure sacrifices the SSA and porosity of supports to some extent. In situ DRIFTS results reveal that the developed porosity of catalyst promotes nitrogen-containing by-products (NHx) transfer and diffusion and avoids their further oxidizing to NOx. The activity of samples prepared by the WI process is lower than that prepared by the IS or GA method due to limited active sites. Comparatively, the Pd/S-2(IS) prepared by the IS method has relative high activity (T-90 of 240 degrees C) and low NOx yield (0.99% at T-90) in n-butylamine oxidation among all materials, exhibiting an attractive prospective in nitrogen-containing VOC environment-friendly elimination.

The Catalytic Performance of Ti-PILC Supported CrO X –ceo 2 Catalysts for N -Butylamine Oxidation

Influence of Interactions Between Chromium and Cerium on Catalytic Performances of CrO X –ceo 2 /Ti-Pilc Catalysts for Deep Oxidation of N -Butylamine

Catalytic Performance of Pillared Interlayered Clays (pilcs) Supported CrCe Catalysts for Deep Oxidation of Nitrogen-Containing VOCs

Effect of Reaction Conditions on Catalytic Performance of Cu/Al-Ce-PILC for Selective Catalytic Reduction of NO by Propylene

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Studies on n-butane isomerization reaction on solid oxide super acid Pt-SO4 2- /ZrO2-Al2O3 catalysts

Influence of synthesis condition on pore structure of Al pillared clays and supported Pd catalysts for deep oxidation of benzene

[Study on Deactivation of Cu/Al-Ce-PILC in the Selective Catalytic Reduction of NO by Propylene].

Promoting effect of Ce added to metal oxide supported on Al pillared clays for deep benzene oxidation

Morphology and Crystal-Plane Effects of CeO2 on TiO2/CeO2 Catalysts During NH3-SCR Reaction

Effect of support acidity on selective catalytic reduction of NO by C3H6 over Cu-based pillared clay catalyst

Copper-impregnated Al–Ce-pillared Clay for Selective Catalytic Reduction of NO by C3H6

Synthesis and Characterization of Aluminum and Al/REE Pillared Clays and Supported Palladium Catalysts for Benzene Oxidation

Preparation, Characterization, and Catalytic Performance of High Efficient CeO2-MnOx-Al2O3 Catalysts for NO Elimination

Spherical-like Pd/SiO2 Catalysts for N-Butylamine Efficient Combustion: Effect of Support Property and Preparation Method

Understanding Structure-Performance Relationships of CoOx/CeO2 Catalysts for NO Catalytic Oxidation: Facet Tailoring and Bimetallic Interface Designing.

Catalytic performance of V2 O5/Ti-Ce-PILC in the selective oxidation of H2 S

Ce-O-P Material Supported CeO2 Catalysts: A Novel Catalyst for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Preparation and Characterization of Ce<sub>0.3</sub>Ti<sub>0.7</sub>O<sub>2</sub> and Supported CuO Catalysts for NO+CO Reaction

The selective catalytic reduction of NO over Ce0.3TiOx-supported metal oxide catalysts

Ti species regulated CuO/CeO2 catalyst for efficient simultaneously NH3-SCR denitration and CO oxidation under oxygen-rich conditions