Abstract:Fischer-Tropsch synthesis (FTS) is a classical topic of great significance because of the approach of post-petroleum times. Recently we found that, taking the advantage of the anchoring effect and intrinsic basicity of nitrogen-doped carbon nanotubes (NCNTs), iron nanoparticles could be conveniently immobilized on the NCNTs without surface pre-modification. The so-constructed Fe/NCNTs catalyst presents the superb catalytic performance in FTS with high selectivity as well as high catalytic activity and stability. In this study, three Fe/NCNTs catalysts were prepared by incipient wetness impregnation method, colloidal method and deposition-precipitation method, denoted as Fe/NCNTs-IWP, Fe/NCNTs-C, and Fe/NCNTs-DP, respectively. The influence of preparation methods on the particle size distribution and morphology, reduction and carbonization of the active species, as well as the FTS catalytic performance were systematically examined. The results indicate that the incipient impregnation method could achieve high dispersion, smaller particles and narrower size distribution [(8 +/- 4) nm], leading to the easier reduction and carbonization of the iron nanoparticles compared with those prepared by the other two methods. The FTS catalytic performance of the Fe/NCNTs-IWP catalyst is much better than those of the Fe/NCNTs-C and the Fe/NCNTs-DP catalysts in terms of the high lower olefins selectivity, high catalytic activity and stability. Colloid method got the different morphologies of iron particles with the average size of (13 +/- 7) nm. The active iron species was susceptible to oxidation during the reaction, which cause poor catalytic activity and stability. The deposition-precipitation method got the largest particles of (19 +/- 11) nm which were difficult to be reduced and carbonized, leading to the sharp decline of the catalytic activity and stability after 15 h reaction. The size-dependence of the catalytic performance for the Fe/NCNTs catalysts in this study are generally in consistent with those in literatures for the iron catalysts supported on carbon nanotubes. These results should be suggestive for exploring the advanced FTS catalysts with the abundant N-doped carbon nanostructures.

FeN Particles Confined Inside CNT for Light Olefin Synthesis from Syngas: Effects of Mn and K Additives

Fischer−Tropsch Synthesis: Influence of Mn on the Carburization Rates and Activities of Fe-Based Catalysts by TPR-EXAFS/XANES and Catalyst Testing

Promotion Effects of Nitrogen Doping into Carbon Nanotubes on Supported Iron Fischer–Tropsch Catalysts for Lower Olefins

Insights into the regulation of FeNa catalysts modified by Mn promoter and their tuning effect on the hydrogenation of CO2 to light olefins

FeN Nanoparticles Confined in Carbon Nanotubes for CO Hydrogenation

Regulation of Ni-CNT Interaction on Mn-Promoted Nickel Nanocatalysts Supported on Oxygenated CNTs for CO2 Selective Hydrogenation.

The promotional effects of carbon nanotube on Fe5C2-ZnO catalysts for CO2 hydrogenation to heavy olefins

Effect of Pressure, H2/CO Ratio and Reduction Conditions on Co-Mn/CNT Bimetallic Catalyst Performance in Fischer-Tropsch Reaction

Enhancing Electrocatalytic CO 2 -to-CO Conversion by Weakening CO Binding through Nitrogen Integration in the Metallic Fe Catalyst

Tuning the Size of TiO2-Supported Co Nanoparticle Fischer-Tropsch Catalysts Using Mn Additions

Restructured Fe−Mn Alloys Encapsulated by N‐doped Carbon Nanotube Catalysts Derived from Bimetallic MOF for Enhanced Oxygen Reduction Reaction

Promotion of manganese on Fe-based catalyst for the production of carbon nanotubes (CNTs) from plastics

Influence of Preparation Methods on Catalytic Performance of Fe/Ncnts Fischer-Tropsch Catalysts

Iron promoted MOF-derived carbon encapsulated NiFe alloy nanoparticles core-shell catalyst for CO2 methanation

Bimetal–Organic Framework-Derived CoMn@C Catalysts for Fischer–Tropsch Synthesis

Fe acting as functionalized auxiliary agents in nitrogen-doped carbon supported Ni-based catalysts for electrocatalytic CO2 Reduction: Effect of valence state

Effect of copper on highly effective Fe-Mn based catalysts during production of light olefins via Fischer-Tropsch process with low CO2 emission

Highly Selective Olefin Production from CO2Hydrogenation on Iron Catalysts: A Subtle Synergy Between Manganese and Sodium Additives

Iron-Potassium on Single-Walled Carbon Nanotubes As Efficient Catalyst for CO2 Hydrogenation to Heavy Olefins

Effect of Mn-dopant on carburization of the Fe3O4 catalysts in Fischer-Tropsch synthesis

Effect of Confinement in Carbon Nanotubes on the Activity of Fischer-Tropsch Iron Catalyst.