Abstract:The effects of the cobalt particle size in the range of 6.5–26.3 nm on the catalyst structural transformation and methane selectivity evolution in Fischer–Tropsch synthesis (FTS) have been investigated. In situ X-ray diffraction experiments revealed that cobalt was maintained as CoO under a reaction environment when initial Co3O4 particles on SiO2 were below 8.4 nm. The large metallic Co particles can keep a stable size and phase state, indicating almost unchanged catalytic activity and methane selectivity. In contrast, small metallic Co or CoO particles show a gradual increase in methane selectivity with time on stream. Stable large metallic Co particles can be explained as the dominant surface high-coordinated Co atoms having a weak binding ability for H2O molecules, which are more difficult to be oxidized into CoO. It is believed that CoO rather than metallic Co atoms could interact with Si-OH groups to form inactive cobalt silicate (Co2SiO4), which leads to a higher methane selectivity and drives a decrease in the particle size during the FTS reaction. ZrO2 as a structural promoter highly dispersed on SiO2 was found to give a milder increase in methane selectivity due to fewer chances of Si-OH interacting with CoO species. Density functional theory (DFT) calculations combined with CO temperature-programmed desorption (CO-TPD), NH3-TPD, CO2-TPD, and Py-IR demonstrate that Co/ZrO2 interfacial sites play a crucial role in enhancing the catalytic activity as the electron accumulation in the interface region not only increases the CO adsorption amount but also promotes the CO dissociation on cobalt sites. At the same time, a higher surface C*/H concentration benefits a lower methane selectivity. ZrO2, which acts as a Lewis acid, can adsorb CO molecules abundantly but weakly by the interaction between Zr4+ cations and O atoms in CO. Especially, for the 15Co(C)/Q15 catalyst with initial CoO particles on SiO2, methane selectivity rapidly increases at an early reaction stage, which originates from easier accessible CoO reacting with Si-OH groups. In addition, both 15Co(C)/Q15 and 15Co(C)/10Zr(I)-Q15 catalysts show the dominant CoO phase, which is active in the FTS reaction. Indeed, the DFT calculations demonstrate that CO activation on the CoO(200) surface via the H-assisted CH2O dissociation pathway exhibits a lower activation energy of 1.21 eV compared to that on the face-centered cubic (fcc) Co(111) surface with an activation energy of 1.42 eV, despite that direct CO dissociation, CHO dissociation, and CHOH dissociation on CoO(200) show higher activation energies. This study provides a prime scientific understanding about regulating catalytic activity and methane selectivity.

Tuning the Size of TiO2-Supported Co Nanoparticle Fischer-Tropsch Catalysts Using Mn Additions

Chemical Imaging of Carbide Formation and Its Effect on Alcohol Selectivity in Fischer Tropsch Synthesis on Mn-Doped Co/TiO2 Pellets

Fischer−Tropsch Synthesis: Influence of Mn on the Carburization Rates and Activities of Fe-Based Catalysts by TPR-EXAFS/XANES and Catalyst Testing

The role of Manganese in CoMnOx Catalysts for Selective Fischer-Tropsch Synthesis

Design and Construction of Size-Controlled CoO/CS Catalysts for Fischer-Tropsch Synthesis

Effect of Mn-dopant on carburization of the Fe3O4 catalysts in Fischer-Tropsch synthesis

Boosting Toluene Combustion in Pt-Co3O4 Catalysts by Directional Tuning Strong Metal-Support Interactions Through Metal-Organic Template Pyrolysis

Bimetal–Organic Framework-Derived CoMn@C Catalysts for Fischer–Tropsch Synthesis

Tuning the Metal–Support Interaction and Enhancing the Stability of Titania-Supported Cobalt Fischer–Tropsch Catalysts via Carbon Nitride Coating

Impact of Inverse Manganese Promotion on Silica-Supported Cobalt Catalysts for Long-Chain Hydrocarbons via Fischer–Tropsch Synthesis

Preparation of Cobalt Nanocrystals Supported on Metal Oxides To Study Particle Growth in Fischer–Tropsch Catalysts

Particle-Size-Dependent Methane Selectivity Evolution in Cobalt-Based Fischer–Tropsch Synthesis

Cobalt Nanoparticles Confined in Carbon Matrix for Probing the Size Dependence in Fischer-Tropsch Synthesis

The role of manganese in CoMnO x catalysts for selective long-chain hydrocarbon production via Fischer-Tropsch synthesis

Tuning the Surface Carbonaceous Species in Syngas-to-Olefin Reaction by Metal-Support Interaction: A Fe-Mn-Al Ternary System Study

Manganese promotion of a cobalt Fischer-Tropsch catalyst to improve operation at high conversion

Tuning the Selectivity of Photothermal CO2 Hydrogenation Through Photo-Induced Interaction Between Ni Nanoparticles and TiO2

Sintering and carbidization under simulated high conversion on a cobalt-based Fischer-Tropsch catalyst; manganese oxide as a structural promotor

Platinum-modulated cobalt nanocatalysts for low-temperature aqueous-phase Fischer-Tropsch synthesis.

Synthesis of SiO2-stabilized FeMn catalysts for catalytic production of liquid fuels: effect of SiO2 position over bimetallic catalysts