Abstract:While the high thermal conductivity, latent heat storage and excellent thermal cycling performance are all important for ceramics used in heat storage, it is difficult to obtain these properties in a single material. In the present study, the heat storage ceramic based on Al-12 wt% Si alloy particles was prepared to achieve these three goals. The alloy particles were pretreated into microcapsules precursor (pre-microcapsules), then mixed with mullite powder and ball clay to prepare green body followed by firing at 1000, 1100, 1200 and 1300 °C. Phase analysis and microstructure observation of the samples after sintering at different temperatures showed that mullite, alumina and Al–Si alloy were the main phases and that the Al-12 wt% Si alloy particles were found in their initial shapes due to their wrapping by the ceramic shell formed during sintering. The test results showed that the sample sintered at 1300 °C with 45 wt % pre-microcapsule content displayed the best performance with a cold crushing strength and a cold modulus of rupture were more than 120 MPa and 65 MPa, respectively. Even after five thermal shock tests, the cold modulus of rupture of the sample was still higher than 50 MPa. More importantly, the thermal conductivity of the sample was as high as 9.36 W m−-1 K−1, the latent heat was 90.84 J g−1 and the latent heat was maintained at 93.4% of the initial value after 3000 thermal cycles. The results meant that these three goals were achieved simultaneously. Moreover, the sensible heat storage capacity was improved by 1.7 times owing to the addition of pre-microcapsules. This heat storage ceramic with Al-12 wt% Si alloy as the phase change material has high potential for use in thermal energy storage systems.

Enhanced Performance of High Temperature Aluminate Cementitious Materials Incorporated with Cu Powders for Thermal Energy Storage

Influence of Fe Powders Replacing Cu Powders on the Thermal and Mechanical Properties of Aluminate Cementitious Thermal Energy Storage Materials at High Temperature

Thermal Properties of Nano-Sio2 Optimized Aluminate Cementitious Composite Cu Powders

Influence of Cu Powders on the Properties and Characteristics of Nano-Mgo Based Aluminate Cementitious Materials

Thermal and Mechanical Properties of Aluminate Cementitious Functional Materials Enriched with Nano-Sio2 for Thermal Energy Storage

Study of Cement-Based Thermal Storage Materials with Fly Ash

Effect of Nano-Mgo on Thermal and Mechanical Properties of Aluminate Cement Composite Thermal Energy Storage Materials

Mechanical and Thermal Properties of Cement Composite Graphite for Solar Thermal Storage Materials

Study on Compressive Strength and Thermal Properties of New Cementitious Thermal Storage Material

Influence of polycarboxylate on thermal properties of cementitious solarthermal storage materials

The Effect of Nanoparticles on the Properties of Calcium Aluminate Cement Pastes at High Temperatures

Preparation and Characterization of Graphite–SiO2 Composites for Thermal Storage Cement-Based Materials

Influence of nano-ZrO2 on the mechanical and thermal properties of high temperature cementitious thermal energy storage materials

High-temperature stability of Cu–20Si alloy-corundum ceramic composite thermal storage materials

Effect of Fe2O3–TiO2-Sm2O3 composite additive on sintering behavior and thermal properties of Al2O3 ceramics for thermal storage

Preparation and characterization of corundum ceramics doped with Fe2O3 and TiO2 for high temperature thermal storage

Preparation and characterization of a heat storage ceramic with Al-12 wt% Si as the phase change material

A novel composite for thermal energy storage from alumina hollow sphere/paraffin and alkali-activated slag

Al-Modified CuO/Cu2O for High-Temperature Thermochemical Energy Storage: from Reaction Performance to Modification Mechanism

Characterization of Supplementary Cementitious Materials and Fibers to Be Implemented in High Temperature Concretes for Thermal Energy Storage (TES) Application

Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage